LD5铝合金超塑性变形的力学特征 被引量:1

Mechanical Behavior of Pretreated Aluminium Alloy LD5 Under Super-plastic Deformation
下载PDF
导出
摘要 研究LD5棒材超塑性变形工艺参数与力学性能的关系。结果表明,LD5铝合金棒材经过495℃×3h固溶、390℃×4.5h过时效+360℃自由镦拔的预处理后,当超塑性变形温度为455℃时,拉伸最佳的变形速率为3.35×10-3mm/s,最高伸长率为475%,相应的流动应力为17MPa。当超塑性变形温度为460℃时压缩最佳的变形速率为2×10-2mm/s,最大伸长率为598%,相应流动应力为21MPa。预处理方法是提高LD5铝合金塑性、降低变形抗力的高效、低成本方法。 The relationship between the technical parameters of LD5 alloy super-plastic deformation and the mechanical performance is investigated. The results show that after pretreatment of solution heat treatment(495℃×3h), over aged disposal(390℃×4.5h), upsetting and drawing(360℃ ), the optimal strain rate of LD5 alloy is 3.35 × 10^-3mm/s, the maximum elongation is 475%, the flow stress is 17MPa at the deformation temperature 455℃. However, at deformation temperature 460℃, the corresponding data of LD5 alloy are 2×10^-2ram/s, 598% and 21MPa, respectively.
作者 李健 韩建业
出处 《有色金属》 CSCD 北大核心 2006年第3期20-22,共3页 Nonferrous Metals
关键词 金属材料 LD5铝合金 超塑性 预处理 变形 力学性能 metal material LD5 alloy super-plastic pretreatment deformation mechanical behavior
  • 相关文献

参考文献6

二级参考文献7

  • 1杨振恒 陈诗荪.金属超塑性与超塑成形[M].西安:西北工业大学出版社,1987.6-7. 被引量:3
  • 2[1]Mishral R S,Mahoney M W,McFadden S X,et al.High Strain rate superplasticity in a friction stir processed 7075 Al alloy[J].Scripta Materialia,1999,42:163-168. 被引量:1
  • 3[2]Kim W J,Kim J K,Park T Y,et al.Enhancement of Strength and Superplasticity in a 6061 Al Alloy Processed by Egual-chamelAngular-Pressing [J].Metallurgical and Materials Transactions A,2002,33A: 3155-3164. 被引量:1
  • 4[3]Kaibyshev R,Kazakulov I,Gromov D,et al.Superplasticity in a 2219 aluminum alloy[J].Scripta Materialia,2001,44:2411-2417. 被引量:1
  • 5[4]Verma R,Ghosh A K,Kim S,Kim C.Grain refinement and superplasticity in 5083Al[J].Materials Science and Engineering,1995,191:143-150. 被引量:1
  • 6黄明宇,王典钧,陆惠生.供应态 LD10 铝合金的超塑性试验研究[J].轻合金加工技术,1998,26(4):33-35. 被引量:4
  • 7连建设,郭威,刘玉文.LY12CZ 铝合金超塑性孔洞长大及其对断裂的影响~*[J].材料科学进展,1991,5(3):215-220. 被引量:6

共引文献9

同被引文献1

  • 1Tong G Q,Chan K C.High-strain-rate superplasticity of an Al-4.4Cu-1.5Mg/21SiCW composite sheet[J].Material Science and Engineering,2000. 被引量:1

引证文献1

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部