摘要
We investigate the temperature dependence of the dielectric constant of BaTiO3 ceramic with coarse to nanograin size under different hydrostatic high pressures up to 5000 bar in the range between room temperature and 200℃. The ferroelectric-to-paraelectric phase transition temperatures Tc are determined from the peak of dielectric constant versus temperature. The values of average grain-size are estimated from the SEM images. It is found that the magnitude of dTc/dp varies considerably from sample to sample depending on grain size. The Curie point Tc of the sample with small grain size decreases more sharply than that of samples with larger one.
We investigate the temperature dependence of the dielectric constant of BaTiO3 ceramic with coarse to nanograin size under different hydrostatic high pressures up to 5000 bar in the range between room temperature and 200℃. The ferroelectric-to-paraelectric phase transition temperatures Tc are determined from the peak of dielectric constant versus temperature. The values of average grain-size are estimated from the SEM images. It is found that the magnitude of dTc/dp varies considerably from sample to sample depending on grain size. The Curie point Tc of the sample with small grain size decreases more sharply than that of samples with larger one.
基金
Supported by the National Key Basic Research and Development Programme of China under Grant No 2002CB613301, and the National Natural Science Foundation of China under Grant Nos 50332020 and 90401003.