摘要
The effect of CO2 and NaCl on the initial stage of atmospheric corrosion of AZ91 magnesium alloy was studied. The observation of surface morphology by optical microscopy （OM）, scanning electron microscopy （SEM） and the analysis of corrosion products by X-ray diffraction （XRD） were integrated to investigate corrosion evolution. The results showed that NaCl stimulated the corrosion by promoting the formation of thin electrolyte film, increasing the conductivity and breaking the protective film in the absence of CO2. The morphology of the corroded samples with deposited NaCl was more homogenous in the presence of CO2. It was suggested that NaCl-induced corrosion was inhibited in the presence of CO2 by the formation of slightly soluble corrosion products containing hydroxy carbonates and hydroxy chlorides that provided a partly protective layer on the surface of the magnesium alloy.
The effect of CO2 and NaCl on the initial stage of atmospheric corrosion of AZ91 magnesium alloy was studied. The observation of surface morphology by optical microscopy （OM）, scanning electron microscopy （SEM） and the analysis of corrosion products by X-ray diffraction （XRD） were integrated to investigate corrosion evolution. The results showed that NaCl stimulated the corrosion by promoting the formation of thin electrolyte film, increasing the conductivity and breaking the protective film in the absence of CO2. The morphology of the corroded samples with deposited NaCl was more homogenous in the presence of CO2. It was suggested that NaCl-induced corrosion was inhibited in the presence of CO2 by the formation of slightly soluble corrosion products containing hydroxy carbonates and hydroxy chlorides that provided a partly protective layer on the surface of the magnesium alloy.
基金
This work was financially supported by the Major State Basic Research Development Program of China (973 Program No. 19990650) and the Materials Science and Engineering Research Center Project of Jiangxi Province of China (No. ZX200401015)