摘要
采用真空热解技术对真空下线路板废渣进行了热解动力学研究,以期为真空热解批量回收处理设备的设计提供理论依据.根据线路板废渣的热失重微分(DTG)曲线,讨论了其在三个失重反应阶段的情况,计算得到反应级数为3,活化能为68.001 kJ/mol,指前因子为4.67×107m in-1.与氮气下线路板的热解相比,真空下的热解反应活化能降低了100 kJ/mol左右.同时,根据计算所得动力学参数模拟的真空热解DTG曲线与实验所得的DTG曲线相一致.
The introduction of vacuum pyrolysis into the treatment of waste print circuit board （WPCB） was first proposed in this paper. In order to lay a theoretical foundation for the batch treatment, the pyrolysis kinetics was investigated. Based on the differential thermo-gravimetry （DTG） curves of WPCB, the three stages of pyrolysis of WPCB were then discussed, and the corresponding kinetic parameters were found, that is, the reaction order is 3, the average activation energy is 68. 001 kJ/mol, and the pre-exponent factor is 4. 67 × 10^7 min^-1. As compared with the pyrolysis in N2, the pyrolysis activation energy in vacuum decreases by about 100 kJ/mol. Furthermore, there is little difference between the simulated DTG curves obtained by computer and by experiments.
出处
《华南理工大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2006年第3期20-22,33,共4页
Journal of South China University of Technology(Natural Science Edition)
基金
广东省科技计划项目(2003E32104)
关键词
线路板废渣
真空热解
动力学
waste print circuit board
vacuum pyrolysis
kinetics