针对半固态触变压铸工艺特点,对国产J1128卧式冷室普通液态压铸机的压射系统和模具系统进行了结构改进,对压铸工艺参数进行了优化选择,并采用半固态专用铝合金AlSi6Mg2和商用铝合金A357开展了大量半固态触变压铸试验研究。结果显示:半固态触变压铸工艺与普通液态压铸有很大的不同,在压射室和模具预热温度分别为100℃和250℃,低压压力为4.0MPa,射料二速工作压力为12MPa,增压压力为20MPa,快压射速度为1.4m/s条件下可获得冲型完好的汽车用铝合金半固态零件。
According to the characteristic of the semi-solid thixo-diecasting processing, the extrusion system and die system of J1128 horizontal die machine made at home were improved ,and the parameters of die-casting processing were optimized,and much experimental investigation on semi-solid thixo-diecasting processing was made by using both semi-solid alloy AlSi6Mg2 and commercial alloy A357. Results show that, the parameters of semi-solid thixo-diecasting processing are different from the ones of traditional die-casting, and sound automobile aluminum alloy part can be obtained when the temperature of container and die are 100℃ and 250℃, respectively,low pressure is 4.0MPa, second extrusion pressure is 12MPa, and fast extrusion velocity is 1.4m/s.
出处
《中国铸造装备与技术》
CAS
2005年第5期23-26,共4页
China Foundry Machinery & Technology
基金
国家高技术研究发展计划(863计划)资助项目(2002AA336080)
关键词
铝合金
半固态
触变压铸
aluminum alloy
semi-solid
thixo-diecasting