为了制备出结合强度较好的生物涂层,采用水热电泳法在碳/碳复合材料表面成功制备了玻璃微纤维增强的羟基磷灰石——壳聚糖(g(f)/HAp-CS)复合涂层,用x-射线衍射仪、透射电子显微镜、扫描电子显微镜、能谱分析仪、红外傅里叶变换分析仪等测试手段对涂层进行了测试和表征,主要研究了水热沉积温度对复合涂层中HAp晶相和涂层显微结构的影响以及HAp涂层的沉积动力学.结果表明:采用玻璃微纤维增强的HAp-CS涂层,致密性和均匀性有了很大提高,显著减少了复合涂层表面的裂纹;随着水热温度的升高,涂层中HAp的衍射峰逐渐增强,表面形貌得到了有效改善,涂层的致密性和均匀性显著提高;涂层的沉积速率随水热温度的升高而加快,其沉积活化能为14.63kJ/mol.
In order to prepare the biological coatings with good bonding strength,the glass microfiber reinforced Hydroxyapatite ( HAp) -CS composite coatings were fabricated by a novel hydrothermal electrophoresis deposition method on the surface of carbon/carbon composite.The coatings were characterized using x-ray diffractometer,transmission election microscope,scanning electron microscope,EDS and FTIR.The influence of hydrothermal temperature on the HAp crystal phase and microstructure of the coating as well as th...
出处
《沈阳工业大学学报》
EI
CAS
2010年第5期487-491,共5页
Journal of Shenyang University of Technology
基金
陕西省教育厅自然科学专项基金资助项目(08JK220)
教育部新世纪优秀人才支持计划(ENCT-06-0893)
陕西科技大学博士科研创新基金资助项目(BS09-09)
陕西科技大学研究生创新基金
陕西省自然科学基金资助项目(SJ08-ZT05)