摘要
利用电化学技术以及表面形貌分析对LaFe11.6Si1.4合金在水溶液中的缓蚀进行研究。结果显示,不同浓度的Na2WO4以及低浓度的NaH2PO4溶液对合金均有显著的缓蚀作用。这主要是由于加入缓蚀剂后,材料的阳极溶解反应被有效抑制,并且在低浓度下由于缓慢的扩散过程阻碍了反应的进行,从而最终抑制腐蚀的发生。
The corrosion inhibition behavior of LaFe11.6Si1.4 alloy in water solution was studied by electrochemical measurements and scanning electron microscope. The results show that the corrosion behavior is inhibited remarkably by Na2WO4 solution with different concentrations or NaH2PO4 solution with low concentration. The inhibition effect is due to the slow anodic dissolution reaction, and the slow diffusion at low concentration of inhibitor.