摘要
以聚丙烯酸为电解质取代传统的液体电解液制备了准固态染料敏化TiO2太阳能电池。该电池具有较好的光电转换性能,在60mW/cm2的模拟光照下(AM1.5),短路电流Isc和开路电压Voc分别为91.5μA/cm2和520mV, 光电转换效率和填充因子分别为0.06%和0.63。
A quasi solid state dye sensitized solar cell was fabricated using acrylic acid polymer as electrolyte. The quasi solid state cell exhibited an optimum photo-eletrochemical behavior. The optimized quasi solid state cell showed the values of 91.5μA/cm^2 for short current photocurrent density, 520mV for open circuit ,0.06% for photoenergy conversion efficiency, and 0.63 for fill factor under simulated solar irradiation (60mW/cm^2,standard AM 1.5).
出处
《人工晶体学报》
EI
CAS
CSCD
北大核心
2005年第3期412-416,共5页
Journal of Synthetic Crystals
基金
国家自然科学基金资助项目(No.50082003)
福建省国际合作项目(No.2001I006)
福建省自然科学基金资助项目(No. E0110026)
华侨大学校基金项目