摘要
为了改善镍铁尖晶石陶瓷的抗热震性、抗弯强度等性能,尝试在合成镍铁尖晶石的过程中添加微量添加剂MnO2,TiO2,V2O5,采用粉末冶金法在1200℃下烧结6h,制备掺杂的镍铁尖晶石惰性阳极材料·研究了不同添加剂和添加量对材料烧结和微观结构的影响以及微观结构对材料抗热震性、抗弯强度等性能的影响·研究结果表明,这些添加剂均能不同程度地促进烧结,提高制品的密度·添加MnO2能够细化晶粒,且粒径分布均匀;而TiO2和V2O5使晶粒变大,且大小分布不均匀·因此只有添加MnO2才能够改善制品的抗弯强度和抗热震性·
In order to improve the properties of resistances to thermal shock and bending of inert anode of NiFe_2O_4 spinel, such additives as MnO_2, TiO_2 and V_2O_5 in trace amount were added to its raw materials and then they were all sintered together at 1200℃ for 6hr, i.e., preparing a doped inert anode by the process of powder metallurgy. The effects of different kinds and amounts of additives on sintering and microstructure of the inert anode were studied, as well as the effect of microstructure and density on its properties, such as the resistances to thermal shock and bending. The results showed that the three additives can benefit the sintering process to different degrees and improve the density. The additive MnO_2 can make grains finer with grain size distributing more uniformly. But TiO_2 or V_2O_5 will make the grains coarser with non-uniform grain size distribution. It means that only MnO_2 can improve the resistances to thermal shock and bending.
出处
《东北大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2005年第6期574-577,共4页
Journal of Northeastern University(Natural Science)
基金
国家高技术研究发展计划项目(2001AA335010)
关键词
镍铁尖晶石
惰性阳极
添加剂
抗热震性
抗弯强度
NiFe_2O_4 spinel
inert anode
additive
resistances to thermal shock
bending