摘要
HGG (Hydroxypropyl guar gum) was synthesized by phase transfer catalysis for the first time. The effects of alkalinity, phase transfer catalyst, etherification, pH value, temperature, reaction time and stirring speed were investigated. An optimal synthetic reaction technology was established, namely, dose of guar gum is 100 g, propylene oxide 40-50 g, HTAC (hexadecyl trimethyl ammonium chloride ) 1.3-1.7 g, pH value 10-10.5, temperature 45-50℃, and reaction time 3-4 hours. The result shows that the improved HGG has high viscosity. Its dissolution speed, content of insoluble residue, colloid light transparency and stability are apparently superior to guar flour.
HGG (Hydroxypropyl guar gum) was synthesized by phase transfer catalysis for the first time. The effects of alkalinity, phase transfer catalyst, etherification, pH value, temperature, reaction time and stirring speed were investigated. An optimal synthetic reaction technology was established, namely, dose of guar gum is 100 g, propylene oxide 40-50 g, HTAC (hexadecyl trimethyl ammonium chloride ) 1.3-1.7 g, pH value 10-10.5, temperature 45-50℃, and reaction time 3-4 hours. The result shows that the improved HGG has high viscosity. Its dissolution speed, content of insoluble residue, colloid light transparency and stability are apparently superior to guar flour.