摘要
Ni nanopowders were successfully prepared in large quantities by anodic arc discharged plasma method with homemade experimental apparatus in inert gas. The particle size, microstructure and morphology of the particles were characterized via X-ray diffractometry(XRD), transmission electron microscopy(TEM) and the corresponding selected area electron diffractometry(SAED). The specific surface area and pore parameters were investigated by nitrogen sorption isotherms at 77 K with Brunauer-Emmett-Teller(BET) equation and Barrett-Joyner-Halenda (BJH) method. The chemical compositions were determined by X-ray energy dispersive spectrometry (XEDS) and element analysis. The experimental results indicate that this method is convenient and effective, and the nanopowders with uniform size, higher purity, weakly agglomerated and spherical chain shape are gotten. The crystal structure of the samples is FCC structure as the bulk materials, the particle size distribution ranges from 20 to 70 nm, and the average particle size is about 46 nm obtained by TEM and confirmed by XRD and BET results. The specific surface area is 14.23 m^2/g, specific pore volume is 0.09 cm^3/g and average pore diameter is 23 nm.
Ni nanopowders were successfully prepared in large quantities by anodic arc discharged plasma method with homemade experimental apparatus in inert gas. The particle size, microstructure and morphology of the particles were characterized via X-ray diffractometry(XRD), transmission electron microscopy(TEM) and the corresponding selected area electron diffractometry(SAED). The specific surface area and pore parameters were investigated by nitrogen sorption isotherms at 77 K with Brunauer-Emmett-Teller(BET) equation and Barrett-Joyner-Halenda (BJH) method. The chemical compositions were determined by X-ray energy dispersive spectrometry (XEDS) and element analysis. The experimental results indicate that this method is convenient and effective, and the nanopowders with uniform size, higher purity, weakly agglomerated and spherical chain shape are gotten. The crystal structure of the samples is FCC structure as the bulk materials, the particle size distribution ranges from 20 to 70 nm, and the average particle size is about 46 nm obtained by TEM and confirmed by XRD and BET results. The specific surface area is 14.23 m^2/g, specific pore volume is 0.09 cm^3/g and average pore diameter is 23 nm.
出处
《中国有色金属学会会刊：英文版》
CSCD
2005年第1期51-56,共6页
Transactions of Nonferrous Metals Society of China
基金
Project(GS012 A52 047) supported by the Bureau of Science & Technology of Gansu Province
China
关键词
阳极电弧等离子体
纳米粉末
镍
颗粒尺寸
anodic arc plasma
Ni nanopowders
particle size
structure
composition