摘要
以Mo粉、Si粉和La2O3为原料,通过自蔓延高温燃烧合成(SHS)的方法制备了La2O3掺杂的MoSi2材料.研究表明,掺杂剂La2O3的加入对MoSi2燃烧合成过程的热力学和动力学具有明显的影响.并通过XRD和SEM对燃烧合成产物的物相组成和形貌进行了分析,发现La2O3的加入对合成产物的物相组成没有明显影响,但可以大大降低合成产物的晶粒尺寸.同时,力学性能研究结果表明,La2O3的加入可以提高MoSi2材料的室温断裂韧性.
La2O3-doped MOSi2 was synthesized by self-propagating high-temperature synthesis. The morphology of the combustion product was investigated by using scanning electron microscopy. The fracture toughness at room temperature was measured by Anstis' mode and the responded microstructure was analyzed by using SEM. The results show that the addition of La2O3 as a doping agent significantly influences the thermodynamics and kinetics of combustion process when compared with the combustion synthesis of molybdenum disilicide alone. The addition of La2O3 can obviously decrease the particle size of the combustion product, and the addition of La2O3 can obviously toughen the matrix.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2004年第6期1334-1338,共5页
Journal of Inorganic Materials
基金
国家"863计划"资助项目(2001AA331040)
上海市科技发展基金(01DJGK016)
国家自然科学基金(50372078)