TEM STUDY OF TWINNING ORIENTATION RELATIOSHIP BETWEEN A AND B MARTENSITE VARIANTS IN A CuZnAl SHAPE MEMORY ALLOY
TEM STUDY OF TWINNING ORIENTATION RELATIOSHIP BETWEEN A AND B MARTENSITE VARIANTS IN A CuZnAl SHAPE MEMORY ALLOY
摘要
A secondary twinning orientation relationship between A and B martensite variants in a CuZnAl shape memory alloy was confirmed under TEM observation.The twin plane, (50),is a linear combination of (8)and(1 0 10)planes,which are twin planes of A:C and A:D type pair respectively.
A secondary twinning orientation relationship between A and B martensite variants in a CuZnAl shape memory alloy was confirmed under TEM observation.The twin plane, (50),is a linear combination of (8)and(1 0 10)planes,which are twin planes of A:C and A:D type pair respectively.
-
1黄跃进.ZnAl3^#RE锌铝合金表面涂敷氧化铝激光重熔的结晶过程[J].上海有色金属,2004,25(1):9-12.
-
2一种新型压铸镁合金[J].铸造技术,2008,29(6):704-704.
-
3田卫平,亢若谷,彭茂公,张家敏.稀土对锌铝合金ZnAl-27性能的改善[J].云南冶金,2002,31(4):45-49. 被引量：7
-
4Zhang, Zhongming, Wang, Jincheng, Xu, Donghui, Lu, Yili, Yang, Gencang, Zhou, Yaohe.Influence of RE Content on Damping Capacity of Alloy ZA27[J].Journal of Rare Earths,1999,17(2):43-46. 被引量：3
-
5刘长瑛,陶小克,孙永昌,王玉红.C/ZnAl-22锌基复合材料阻尼性能[J].天津理工学院学报,2003,19(1):62-64.
-
6毛杰,宋进兵,邓畅光,黄科.氧化铝涂层的超音速等离子喷涂参数影响及硬度分析[J].表面技术,2014,43(4):110-114. 被引量：14
-
7刘安强,肖葵,李晓刚,袁建鹏.Zn和ZnAl合金涂层在西沙严酷海洋大气环境下的腐蚀行为的比较[J].热喷涂技术,2015,7(4):46-52. 被引量：6
-
8严彪,张晴,严鹏飞,赵冠楠.热喷涂制备ZnAl涂层防腐性能研究[J].上海有色金属,2014,35(4):139-144.
-
9Z.S. Zhu,N.P.Chen,J.L. Gu and M.G. Yan(1)Institute of Aeronautical Materials, P.O. Box 8115, Beijing 100095, China 2)Department of Materials Science and Engineering, Tsinghua University, Beijing 100084, ).ORIENTATION VARIANT SELECTION AND ITS EFFECTING FACTORS IN TITANIUM SHEET[J].Acta Metallurgica Sinica(English Letters),1996,9(6):601-605. 被引量：2
-
10Qingan ZHANG and Nanju GU (Hebei Institute of Technology Tianjin, 300130, China)(East China Institute of Metallurgy,Ma’anshan, 243002, China).Crossed Micro-bands in the Martensite Variant Pairs of a Thermomechanically Trained Cu-Zn-Al Alloy[J].Journal of Materials Science & Technology,1995,11(6):418-420.