The thermal behavior, miscibility, crystallite conformation and thermal stability ofcrosslinked(CL-) PVA/PVP blends were studied by DSC and TG methods, respectively. DSCresults showed that in the blend, the crystallinity,T_m and T_c of PVA were obviously lower thanthose of pure PVA; the crystal growth changed from three dimensional to two dimensional andonly a single T_g was detected. These facts demonstrated that this crystalline and amorphousblend have good miscibility. TG curves showed that providing the quantity of K_2S_2O_8 added ismore than 3 wt%,in the blends PVA will form a stable CL-network, whose thermal degradationtemperature was near to that of PVP. But crosslinking reaction will not take place for PVP. Theprocesses of thermal degradation of CL-blends are based on combining both the thermaldegradation of PVP and that of PVA crosslinked with corresponding quantity of K_2S_2O_8 CL-agent, respectively. The UV measurements showed that 75 wt% of PVP may be remained in CL-blend hydrogelscrosslinked by adding (3--5 wt% )K_2S_2O_8. This is mainly due to the stable CL-network formed and the good compatibility and properentanglement between the composites in the CL-blends.
The thermal behavior, miscibility, crystallite conformation and thermal stability ofcrosslinked(CL-) PVA/PVP blends were studied by DSC and TG methods, respectively. DSCresults showed that in the blend, the crystallinity,T_m and T_c of PVA were obviously lower thanthose of pure PVA; the crystal growth changed from three dimensional to two dimensional andonly a single T_g was detected. These facts demonstrated that this crystalline and amorphousblend have good miscibility. TG curves showed that providing the quantity of K_2S_2O_8 added ismore than 3 wt%,in the blends PVA will form a stable CL-network, whose thermal degradationtemperature was near to that of PVP. But crosslinking reaction will not take place for PVP. Theprocesses of thermal degradation of CL-blends are based on combining both the thermaldegradation of PVP and that of PVA crosslinked with corresponding quantity of K_2S_2O_8 CL-agent, respectively. The UV measurements showed that 75 wt% of PVP may be remained in CL-blend hydrogelscrosslinked by adding (3--5 wt% )K_2S_2O_8. This is mainly due to the stable CL-network formed and the good compatibility and properentanglement between the composites in the CL-blends.