The effects of addition of chromium or boron on room temperature tensile properties,fracture behavior and susceptibility to test environments (air vs. vacuuwi of forged Fe3Al have been investigated. The results indicated that both chromium and boron result in increasing room temperuture ductility and fracture strength of the Fe3Al alloy whether tested in air or in vacuum. The susceptibility to test envimnment was described with the embrittlement index I: I=(δv-δA)/δv. The embrittlement indexes, for Fe-30Al, Fe-30Al-4Cr and Fe-30Al-0. 13B (at. %), are 24%, 37% and 29%,respectively. Scanning electron microscope examination of fracture surface revealed that the fracture mode of the three alloys remains unchanged, and all of them exhibited a transgranular cleavage fracture mode when tested in vacuum or air.
The effects of addition of chromium or boron on room temperature tensile properties,fracture behavior and susceptibility to test environments (air vs. vacuuwi of forged Fe3Al have been investigated. The results indicated that both chromium and boron result in increasing room temperuture ductility and fracture strength of the Fe3Al alloy whether tested in air or in vacuum. The susceptibility to test envimnment was described with the embrittlement index I: I=(δv-δA)/δv. The embrittlement indexes, for Fe-30Al, Fe-30Al-4Cr and Fe-30Al-0. 13B (at. %), are 24%, 37% and 29%,respectively. Scanning electron microscope examination of fracture surface revealed that the fracture mode of the three alloys remains unchanged, and all of them exhibited a transgranular cleavage fracture mode when tested in vacuum or air.