Theinitialstageofagingtransformationin Al 2 27% Li 2 68 % Cu 0 11% Zr 0 13% Ceal loy at100℃wasstudied by meansof x ray diffraction.It wasconcludedthatordering of Liatom happens whenthealloyissolution treated andquenched, and beforetheformationofδ’ phasethereexitscontinuous phasetransformation processes, namely ordering ,spinodal de composition and both coexistence. Gunier Preston zone was not found in the aging process ofthestudied alloy.
Theinitialstageofagingtransformationin Al 2 27% Li 2 68 % Cu 0 11% Zr 0 13% Ceal loy at100℃wasstudied by meansof x ray diffraction.It wasconcludedthatordering of Liatom happens whenthealloyissolution treated andquenched, and beforetheformationofδ’ phasethereexitscontinuous phasetransformation processes, namely ordering ,spinodal de composition and both coexistence. Gunier Preston zone was not found in the aging process ofthestudied alloy.