According to GBJ82-85 test method for frost resistance of concrete,four-point bending tests were used to examine the effects of mineral admixture(silica fume and fly ash)on fracture toughness,fracture energy and dynamic elastic modulus of concrete subjected to rapid freeze-thaw cycles The microstructure of the concrete was also analyzed.The results show that with the increase of the number of freeze-thaw cycles,the fracture toughness of concrete,and the loss of fracture energy as well as the l0ss of relative dynamic elastic modulus showed a downward trend.The air content of fresh concrete is the most important parameter to improve frost resistance of concrete There existed distinct difference for silica fume and fly ash to enhance fracture performance and microstructure of the concrete under freeze-thaw cycles.The l0ss of fracture energy and the loss of relative dynamic elastic modulus kept a good linear relationship.
According to GBJ82-85 test method for frost resistance of concrete,four-point bending tests were used to examine the effects of mineral admixture(silica fume and fly ash)on fracture toughness,fracture energy and dynamic elastic modulus of concrete subjected to rapid freeze-thaw cycles The microstructure of the concrete was also analyzed.The results show that with the increase of the number of freeze-thaw cycles,the fracture toughness of concrete,and the loss of fracture energy as well as the l0ss of relative dynamic elastic modulus showed a downward trend.The air content of fresh concrete is the most important parameter to improve frost resistance of concrete There existed distinct difference for silica fume and fly ash to enhance fracture performance and microstructure of the concrete under freeze-thaw cycles.The l0ss of fracture energy and the loss of relative dynamic elastic modulus kept a good linear relationship.