Fracture theory based on the concept of characteristic fracture length of materials 被引量:2

Fracture theory based on the concept of characteristic fracture length of materials
原文传递
导出
摘要 Fracture theory is a classic,but not a well-dealt with,difficulty in solid mechanics. This paper has proposed the concept of characteristic fracture length of materials from the fact that fracture happens with area failure rather than point failure in materials. A unified theory is then proposed,which can be applied both to smooth and defected materials (whether with micro or macro defects). Brittle fracture tests with specimens of different sizes of holes are carried out to examine the fracture theory. It is found that the fracture stresses obtained by experiments agree well with those predicated by the presented fracture theory. Though the brittle fracture is the focus of the paper,the concept of characteristic length can be easily extended to fatigue or other failure problems. Fracture theory is a classic, but not a well-dealt with, difficulty in solid mechanics. This paper has proposed the concept of characteristic fracture length of materials from the fact that fracture happens with area failure rather than point failure in materials. A unified theory is then proposed, which can be applied both to smooth and defected materials (whether with micro or macro defects). Brittle fracture tests with specimens of different sizes of holes are carried out to examine the fracture theory. It is found that the fracture stresses obtained by experiments agree well with those predicated by the presented fracture theory. Though the brittle fracture is the focus of the paper, the concept of characteristic length can be easily extended to fatigue or other failure problems.
出处 《Science China(Physics,Mechanics & Astronomy)》 SCIE EI CAS 2009年第12期2041-2046,共6页 中国科学:物理学、力学、天文学(英文版)
基金 Supported by the National Natural Science Foundation of China (Grant No. 10772116)
关键词 FRACTURE THEORY strength CHARACTERISTIC LENGTH SIZE effect BRITTLE FRACTURE fracture theory strength characteristic length size effect brittle fracture
  • 相关文献

参考文献14

  • 1卓杨,许金泉.基于分子动力学的结合材料界面破坏准则[J].力学季刊,2007,28(1):1-7. 被引量:4
  • 2G. C. Sih.Strain-energy-density factor applied to mixed mode crack problems[J]. International Journal of Fracture . 1974 (3) 被引量:1
  • 3Cadario A,Alfredsson B.Fatigue growth of short cracks in Ti-17: Experiments and simulations. Engineering Fracture Mechanics . 2007 被引量:1
  • 4Atzori B,Lazzarin P,Meneghetti G.Fracture mechanics and notchsensitivity. Fat Fract Eng Mater Struc . 2002 被引量:1
  • 5Torres Y,Bermejo R,Llanes L, et al.Influence of notch radius and R-curve behavior on the fracture toughness evaluation of WC-Co cemented carbides. Engineering Fracture Mechanics . 2008 被引量:1
  • 6Taylor D.The theory of critical distances. Engineering Fracture Mechanics . 2008 被引量:1
  • 7Zhang X B,Li J.A failure criterion for brittle and quasi-brittle mate- rials under any level of stress concentration. Engineering Fracture Mechanics . 2008 被引量:1
  • 8Shi G C.Mechanics of Fracture. . 1972 被引量:1
  • 9Kitagawa H,Yuuki R,Tohgo K.Fatigue crack propagation behavior under mixed mode condition. Transactions of the JSME . 1981 被引量:1
  • 10Yu M H.Generalized Plasticity. . 2005 被引量:1

二级参考文献16

  • 1樊康旗,贾建援.经典分子动力学模拟的主要技术[J].微纳电子技术,2005,42(3):133-138. 被引量:30
  • 2Baskes M I,Angelo J E,Bison C L.Atomistic calculations of composite interfaces[J].Modell Simul Mater Sci Engng,1994,(2):505 -518. 被引量:1
  • 3Kitamura T,Hirakate H,Satake Y.Applicability of fracture mechanics on brittle delamination of nanoscale film edge[J].JSME International Journal,Series A,2004,47(2):106-112. 被引量:1
  • 4Ikeda T,Miyazaki N.Mixed mode fracture criterion of interface crack between dissimilar material[J].Engineering Fracture Mecanics,1998,59(6):725-735. 被引量:1
  • 5Girifalco L A,Weizer V G.Application of the Morse potential function to cubic metals[J].Phys Rev,1959,114:687-690. 被引量:1
  • 6Cheung K S,Yip S.Atomic-level stress in an inhomogeneous system[J].ASME J Appl Phys,1991,70:5688-5690. 被引量:1
  • 7Fuller E R,Thomson R M.Lattice theories of fracture[A].In:Bradt R C,Evans A G,Hasselman D P H,Lange F F(Eds.).Fracture Mechanics of Ceramics[C].New York:Plenum 1978,4:507. 被引量:1
  • 8Chang R.An atomistic study of fracture[J].Int J Fract Mech,1970,6:111-118. 被引量:1
  • 9Sinclair J E,lawn B R.An atomistic study of cracks in diamond-structure crystals[J].Proc R Soc London,Ser A,1972,329:83-103. 被引量:1
  • 10Abraham F,Brodbeck D,Rafey R,Rudge W.Instability dynamics of fracture:a computer simulation investigation[J].Phys Rev Lett,1994,73:272-275. 被引量:1

共引文献3

同被引文献8

引证文献2

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部