The effect of coagulation temperature on the morphology, microstructures and mechanical properties of dihydroxy poly(p-phenylene benzobisoxazole) (DHPBO) fibers was investigated during dry-jet wet-spinning process, in which the coagulation bath concentration and drawn ratio were kept as 10 wt% of PPA in water and 1.7, respectively. The structures and mechanical properties of the as-spun DHPBO fibers were characterized by FTIR, XRD, SEM, and single fiber tensile testing. The results indicated that in PPA/H<SUB>2</SUB>O coagulation system, when the coagulation temperature was 25°C, highly crystallized DHPBO as-spun fibers possessing fine crystallites, circular and smooth morphology, and excellent mechanical properties could be achieved.