摘要
A series of Pr-Co thin films were deposited on the Si (100) substrates with Cr underlayer by magnetron sputtering. The effects of both the post-annealing temperature and the annealing time on the microstructure and magnetic properties for the Pr-Co films were studied systemati- cally. The as-deposited Pr-Co thin films are mostly amorphous and tend to crystallize after annealing at temperatures above 600 C. When the annealing time is increased, the films show a complicated structure with various phases coexisting. Accordingly, the as-deposited film and low temperature annealed films are soft magnets and films annealed at temperatures beyond 600 C tend to be hard magnets. When the annealing time is increased from 5 min to 2 h, the films transfer from hard magnets to soft again. The sample annealed at 600 C for 10 min shows the largest coercivity of 0.59 T.
基金
supported by the National Natural Science Foundation of China (No. 50801023)
Educational Commission of Hubei Province (No. D20091008)
the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry (SRF for ROCS, SEM)