摘要
采用耐尔(纳米银溶液浸渍法制备医用载银粘胶纤维。讨论了在固定浴比下,纳米银溶液浓度、浸渍温度和浸渍时间对载银粘胶纤维银含量的影响;测定了不同银含量的载银粘胶纤维的抗菌性能。结果表明:在固定浴比下,提高纳米银溶液浓度、提高浸渍温度和延长浸渍时间,可提高载银粘胶纤维的银含量。当载银粘胶纤维上的银含量达到100 mg/kg时,对大肠埃希菌(大肠杆菌)和金黄色葡萄球菌的抗菌率能达到99%以上;当载银粘胶纤维上的银含量达到500 mg/kg时,对白念珠菌的抗菌率能达到99%以上。
Medical silver-loaded viscose fiber is prepared through dipping with Naier nano-silver solution.Under fixed bath ratio,effect of nano-silver solution dosage,dipping temperature and dipping time on silver content of the loaded fiber is discussed.The antibacterial property of the silver-loaded fiber is tested.Result shows that with a fixed bath ratio,the silver content loaded on the viscose fiber increased with the concentration of Naier nano-silver solution,the dipping temperature and time.The antibacterial rate of the fiber against Escherichia coli and Staphylococcus aureus can reach above 99% with 100 mg/kg silver,and the antibacterial rate against Candida albicans can reach above 99% with 500 mg/kg silver.
出处
《印染》
北大核心
2012年第4期34-36,共3页
China Dyeing and Finishing
基金
2011年江苏省大学生实践创新训练计划项目,苏教高[2011]25号
张家港市科技孵化项目,编号:ZFH1004
江苏省“青蓝工程”资助,苏教师[2010]27号
关键词
抗微生物整理
纳米银
抗微生物性
粘胶纤维
antimicrobial finish
nano silver
antimicrobial property
viscose fiber