摘要
在无镍白铜(CuMnZn)中分别添加微量稀土Ce(0.04%,0.06%,0.08%),研究稀土Ce含量及加工工艺参数对铸态、热轧态和冷轧态组织及性能的影响。探索用无镍白铜(CuMnZn)替代目前广泛使用的弹性合金材料——锌白铜的可行性。研究结果显示:当稀土含量小于0.04%时,随合金中稀土Ce含量的增加,铸态合金的α晶粒尺寸减少,细化晶粒,提高合金的抗拉强度、伸长率,且合金具有较好的冷加工性能。当稀土Ce含量超过0.04%后,合金的晶粒又有长大的趋势。材料的性能在0.04%左右达到峰值,随着稀土Ce含量的增加,其性能呈下降趋势。对含0.04%稀土Ce的无镍白铜(CuMnZn)合金,采用合理加工工艺和热处理制度加工而成的0.3 mm厚的带材的洛氏硬度、抗拉强度及伸长率分别为85HRB,567.4 MPa及5%,与Y状态BZn15-20材料的性能相当,满足弹性材料的使用要求。且无镍白铜(CuMnZn)合金中的元素都是国内富有元素,可有效降低成本,具有实用价值。
The effect of different content of Ce(0.04%,0.06%,0.08%) and process technical parameters on the structure and mechanical characteristics of CuMnZn nickel-free copper alloy of ingot as-cast,strip of hot-rolled and cool-rolled was studied.The substitute possibility of nickel-free copper alloy for Zinc-nickel-copper alloy was investigated.The results showed that when the content of Ce was less than 0.04%,with the increase of Ce content,the size of α phase deceased in the as-cast,the tensile strength and hardn...
出处
《稀有金属》
EI
CAS
CSCD
北大核心
2010年第6期823-827,共5页
Chinese Journal of Rare Metals
基金
江西省自然基金(2009GZC0048)资助项目
关键词
无镍白铜
稀土Ce
带材
抗拉强度
伸长率
nickle-free copper alloy
Ce
strip
tensile strength
elongation