To characterize the effects of alloying elements on inclusion dissolution of titanium nitride, the content profiles of elements around TiN/Ti boundary α phase regions in liquid titanium alloys have been experimentally carried out. Four kinds of commercial alloys of CpTi, Ti64, Ti17 and Ti6242 containing different α stabilizing or β stabilizing elements are examined through artificially embedding the TiN sponge particle into liquid alloys in VAR conditions. The content profiles of nitrogen and alloying elements around TiN/Ti boundary were measured by WDX and microprobe for as cast samples. The content profiles of nitrogen and alloying elements around N containing solid in α Ti region of these alloys show a common features of a steep change. In particular, the content profiles of elements for Ti6242 demonstrate unique change of a more gentle change tendency and further deeper into the alloy matrix. The experiment results show that, the differences among composite effects of alloying elements in different alloys within nitrogen induced diffusion α region result in different dissolution and diffusion behaviors to overcome the α phase region barriers.
To characterize the effects of alloying elements on inclusion dissolution of titanium nitride, the content profiles of elements around TiN/Ti boundary α phase regions in liquid titanium alloys have been experimentally carried out. Four kinds of commercial alloys of CpTi, Ti64, Ti17 and Ti6242 containing different α stabilizing or β stabilizing elements are examined through artificially embedding the TiN sponge particle into liquid alloys in VAR conditions. The content profiles of nitrogen and alloying elements around TiN/Ti boundary were measured by WDX and microprobe for as cast samples. The content profiles of nitrogen and alloying elements around N containing solid in α Ti region of these alloys show a common features of a steep change. In particular, the content profiles of elements for Ti6242 demonstrate unique change of a more gentle change tendency and further deeper into the alloy matrix. The experiment results show that, the differences among composite effects of alloying elements in different alloys within nitrogen induced diffusion α region result in different dissolution and diffusion behaviors to overcome the α phase region barriers.
出处
《中国有色金属学会会刊：英文版》
CSCD
2001年第5期738-742,共5页
Transactions of Nonferrous Metals Society of China