Hydrogen storage properties of Laves phase Ti_(1-x)Zr_x(Mn_(0.5)Cr_(0.5))_2 alloys 被引量:4

Hydrogen storage properties of Laves phase Ti_(1-x)Zr_x(Mn_(0.5)Cr_(0.5))_2 alloys
下载PDF
导出
摘要 The activation behaviors and hydrogen storage properties of the Laves phase Ti1-xZrx(Mn0.5Cr0.5)2 (x=0, 0.1, 0.2, 0.32, 0.5) alloys were investigated by the pressure-composition-temperature (P-C-T) measurements. All the studied alloys show the single C14-type Laves phase structure based on the XRD data. Except for the alloys with very low Zr content of x=0 and x=0.1, all these alloys can be fully activated. The P-C isotherms of the activated alloys show that, the introduction of Zr induces the decrease of the equilibrium pressures and the steeper plateaus. As the x increases, the maximum hydrogen absorption also increases, whereas the desorption of hydrogen decreases. These two effects result in a maximum reversible hydrogen storage capacity of H/M=3.03 for the alloy at x=0.32. Furthermore, the well-defined plateau associated with the smallest hysteresis also appears at x=0.32. The activation behaviors and hydrogen storage properties of the Laves phase Ti1-xZrx(Mn0.5Cr0.5)2 (x=0, 0.1, 0.2, 0.32, 0.5) alloys were investigated by the pressure-composition-temperature (P-C-T) measurements. All the studied alloys show the single C14-type Laves phase structure based on the XRD data. Except for the alloys with very low Zr content of x=0 and x=0.1, all these alloys can be fully activated. The P-C isotherms of the activated alloys show that, the introduction of Zr induces the decrease of the equilibrium pressures and the steeper plateaus. As the x increases, the maximum hydrogen absorption also increases, whereas the desorption of hydrogen decreases. These two effects result in a maximum reversible hydrogen storage capacity of H/M=3.03 for the alloy at x=0.32. Furthermore, the well-defined plateau associated with the smallest hysteresis also appears at x=0.32.
出处 《Rare Metals》 SCIE EI CAS CSCD 2006年第z1期218-223,共6页 稀有金属(英文版)
基金 This work was supported by the National Natural Science Foundation of China (No.50371086).
关键词 Laves phase hydrogen storage alloys activation behavior P-C isotherms Laves phase hydrogen storage alloys activation behavior P-C isotherms
  • 相关文献

参考文献10

  • 1[1]Huang T.Z.,Wu Z.,Yu X.B.,et al.,Hydrogen absorption-desorption behavior of zirconium-substituting Ti-Mn based hydrogen storage alloys.Intermetallic,2004,12:91. 被引量:1
  • 2[2]Liu B.H.,Kim D.M.,Lee K.Y.,et al.,Hydrogen storage properties of TiMn2-based alloys.J.Alloys Comp.,1996,240:214. 被引量:1
  • 3[3]Klyamkin S.N.,Verbetsky V.N.,and Demidov V.A.,Thermodynamicsof hydride formation and decomposition for TiMn2-H2 system at pressure up to 2000 atm.J.Less-Common Met.,1994,205:L1. 被引量:1
  • 4[4]Au M.,Pourarian F.,Sankar S.G.,et al.,TiMn2-based alloys as high hydrogen storage materials.Mater.Sci.Engi.,1995,B33:53. 被引量:1
  • 5[5]Bobet J.L.,and Darriet B.,Relationship between hydrogen sorption properties and crystallography for TiMn2 based alloys.Int.J.Hydrogen Energy,2000,25:767. 被引量:1
  • 6[6]Oesterreicher H.,and Bitter H.,Studies of hydrogen formation in Ti1-xZrxMn2.Mat.Res.Bull.,1978,13:83. 被引量:1
  • 7[7]Jacob I.,Stern A.,Moran A.,et al.,Hydrogen absorption in(ZrxTi1-x)B2(B≡Cr,Mn)and the phenomenological model for the absorption capacity in pseudo-binary Laves-phase compounds.J.Less-Common Met.,1980,73:369. 被引量:1
  • 8[8]Kisi E.H.,Buckley C.E.,and Gray E.M.,The hydrogen activationof LaNi5.J.Alloys Comp.,1992,185:369. 被引量:1
  • 9[9]Lundin C.E.,Lynch F.E.,and Magee C.B.,A correlation between the interstitial hole sizes in intermetallic compounds and the thermodynamic properties of the hydrides formed from those compounds.J.Less-Common Met.,1977,56:19. 被引量:1
  • 10[10]Ivey D.G.,and Northwood D.O.,Storing energy in metal hydrides:a review of the physical metallurgy.J.Mater.Sci.,1983,18:321. 被引量:1

同被引文献31

引证文献4

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部