We report that the corrosion resistance of Mg is significantly improved by adding 0.05wt%Sc.Corrosion rates evaluated from weight loss values after room-temperature immersion in 0.6 M NaCl solution for two weeks were 0.27 and 4.0 mm y^(-1)for the high-purity Mg samples with and without microalloyed 0.05wt%Sc,respectively.The beneficial effect of Sc microalloying on the corrosion resistance of Mg is discussed in connection with Sc-induced microstructural modifications.