The phase constituent evolution of Mg-Zn-Y-Zr alloys with the mole ratio of Y to Zn both in the as-cast and as-annealed states at the Mg-rich corner was investigated by XRD and SEM/EDS analysis and was further explain...The phase constituent evolution of Mg-Zn-Y-Zr alloys with the mole ratio of Y to Zn both in the as-cast and as-annealed states at the Mg-rich corner was investigated by XRD and SEM/EDS analysis and was further explained from the ternary phase diagram calculation. The results show that the formation of the secondary phases in Mg-Zn-Y-Zr alloys firmly depends on the mole ratio of Y to Zn, and X （Mg 12 YZn）-phase, W （Mg 3 Y 2 Zn 3 ）-phase and I （Mg 3 YZn 6 ）-phase come out in sequence as the ratio of Y to Zn decreases. The mole ratios of Y to Zn with the corresponding phase constituent are suggested quantitatively as follows： the phase constituent is α-Mg ＋ I when the mole ratio of Y to Zn is about 0.164; α-Mg ＋ I ＋W when the mole ratio of Y to Zn is in the range of 0.164 0.33;α-Mg ＋W when the mole ratio of Y to Zn is about 0.33; α-Mg ＋W＋X when the mole ratio of Y to Zn is in the range of 0.33 1.32; and α-Mg ＋X when the mole ratio of Y to Zn is about 1.32. The results also offer a guideline for alloy selection and alloy design in Mg-Zn-Y-Zr system.展开更多
Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electro...Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electron microscope （SEM）, X-ray diffractometer （XRD） and energy dispersive spectrometer （EDS）. The results show that yttrium and/or strontium additions produce a strong grain refining effect in LA141 alloy. The mean grain sizes of the alloys with addition of Y and/or Sr are reduced remarkably from 600 to 500, 260, 230 μm, respectively. Al 2 Y, Al 4 Sr and Mg 17 Sr 2 phases with different morphologies are verified and exist inside the grain or at the grain boundaries, thus possibly act as heterogeneous nucleation sites and pin up grain boundaries, which restrain the grain growth.展开更多
The effects of texture and abnormal large grains on the plastic anisotropy and fracture behavior of hot-rolled AZ31 magnesium alloy were investigated. Uniaxial tensile deformation behaviors of samples with tensile axi...The effects of texture and abnormal large grains on the plastic anisotropy and fracture behavior of hot-rolled AZ31 magnesium alloy were investigated. Uniaxial tensile deformation behaviors of samples with tensile axis tilting 0°, 15°, 30°, 45°, 60°, 75° and 90° to normal direction （ND） respectively were addressed. Tensile deformation anisotropy was observed for samples with different angles to ND. The results show that the specimens with the angle from 0° to 30° exhibit relatively lower yielding strength due to the {1 012}extension twinning. However, basal slip and prismatic slip are the dominant deformation modes for the specimens with angles larger than 45°. Macro-fractures are parallel to the length direction of abnormal large grains in the specimens with angles less than 60°, while those are serrated fracture edge for specimens with angles 75° and 90°.展开更多
The as-cast microstructure and Sr-containing phases in the AZ31 magnesium alloys with different Sr contents （0%, 0.3%, 2.5% and 5.0%, mass fraction） were investigated. The results indicate that after adding Sr to th...The as-cast microstructure and Sr-containing phases in the AZ31 magnesium alloys with different Sr contents （0%, 0.3%, 2.5% and 5.0%, mass fraction） were investigated. The results indicate that after adding Sr to the AZ31 magnesium alloy, the dendrite/grain size is decreased, and with the Sr content increasing from 0 to 5.0%, the dendrite becomes finer, the dendrite morphology becomes more passive and the distribution of alloying phases at dendrite/grain boundary is dispersed. Furthermore, the morphology of the β-Mg 17 Al 12 phase in the alloy with addition of 0.3%Sr changes from continuously irregular strip-like shape to discontinuously irregular strip-like shape and/or fine granule-like shape. At the same time, some lamella-like eutectic phases are found in the alloys with additions of 2.5% Sr and 5.0% Sr, and the lamella spacing in the alloy with addition of 5.0% Sr is finer. Adding high Sr content to the AZ31 alloy can bring the new ternary eutectic and/or divorced eutectic phase of Mg 11 Al 5 Zn 4 in the alloy, and the Mg 17 Sr 2 and Mg 2 Sr phases are formed in the alloys with additions of 2.5% Sr and 5.0% Sr.展开更多
基金Project(50725413)supported by the National Natural Science Foundation of China
文摘The phase constituent evolution of Mg-Zn-Y-Zr alloys with the mole ratio of Y to Zn both in the as-cast and as-annealed states at the Mg-rich corner was investigated by XRD and SEM/EDS analysis and was further explained from the ternary phase diagram calculation. The results show that the formation of the secondary phases in Mg-Zn-Y-Zr alloys firmly depends on the mole ratio of Y to Zn, and X （Mg 12 YZn）-phase, W （Mg 3 Y 2 Zn 3 ）-phase and I （Mg 3 YZn 6 ）-phase come out in sequence as the ratio of Y to Zn decreases. The mole ratios of Y to Zn with the corresponding phase constituent are suggested quantitatively as follows： the phase constituent is α-Mg ＋ I when the mole ratio of Y to Zn is about 0.164; α-Mg ＋ I ＋W when the mole ratio of Y to Zn is in the range of 0.164 0.33;α-Mg ＋W when the mole ratio of Y to Zn is about 0.33; α-Mg ＋W＋X when the mole ratio of Y to Zn is in the range of 0.33 1.32; and α-Mg ＋X when the mole ratio of Y to Zn is about 1.32. The results also offer a guideline for alloy selection and alloy design in Mg-Zn-Y-Zr system.
基金Project(50725413)supported by the National Natural Science Foundation of ChinaProject(2010CSTC-BJLKR)supported by Chongqing Science and Technology Commission, ChinaProject(CDJXS10132203)supported by the Fundamental Research Funds for the Central Universities,China
文摘Mg-14Li-1Al （LA141）, LA141-0.3Y, LA141-0.3Sr, and LA141-0.3Y-0.3Sr alloys were prepared in an induction furnace in the argon atmosphere. The microstructures of these alloys were investigated through scanning electron microscope （SEM）, X-ray diffractometer （XRD） and energy dispersive spectrometer （EDS）. The results show that yttrium and/or strontium additions produce a strong grain refining effect in LA141 alloy. The mean grain sizes of the alloys with addition of Y and/or Sr are reduced remarkably from 600 to 500, 260, 230 μm, respectively. Al 2 Y, Al 4 Sr and Mg 17 Sr 2 phases with different morphologies are verified and exist inside the grain or at the grain boundaries, thus possibly act as heterogeneous nucleation sites and pin up grain boundaries, which restrain the grain growth.
基金Project(2007CB613703)supported by the National Basic Research Program of ChinaProject(CDJXS11132227)supported by the Fundamental Research Funds for the Central Universities,China
文摘The effects of texture and abnormal large grains on the plastic anisotropy and fracture behavior of hot-rolled AZ31 magnesium alloy were investigated. Uniaxial tensile deformation behaviors of samples with tensile axis tilting 0°, 15°, 30°, 45°, 60°, 75° and 90° to normal direction （ND） respectively were addressed. Tensile deformation anisotropy was observed for samples with different angles to ND. The results show that the specimens with the angle from 0° to 30° exhibit relatively lower yielding strength due to the {1 012}extension twinning. However, basal slip and prismatic slip are the dominant deformation modes for the specimens with angles larger than 45°. Macro-fractures are parallel to the length direction of abnormal large grains in the specimens with angles less than 60°, while those are serrated fracture edge for specimens with angles 75° and 90°.
基金National Natural Science Foundation of China(51571044)National Key Research and Development Program of China(2016YFB0301102)Chongqing Foundation and Advanced Research Project(cstc2015jcyjBX0081)
基金Project(50725413)supported by the National Natural Science Foundation of ChinaProject(2007CB613704)supported by the NationalBasic Research Program of China+1 种基金Project(2010CSTC-BJLKR)supported by Chongqing Science and Technology Commission,ChinaProject(CDJZR11130024)supported by the Fundamental Research Funds for the Central Universities,China
文摘The as-cast microstructure and Sr-containing phases in the AZ31 magnesium alloys with different Sr contents （0%, 0.3%, 2.5% and 5.0%, mass fraction） were investigated. The results indicate that after adding Sr to the AZ31 magnesium alloy, the dendrite/grain size is decreased, and with the Sr content increasing from 0 to 5.0%, the dendrite becomes finer, the dendrite morphology becomes more passive and the distribution of alloying phases at dendrite/grain boundary is dispersed. Furthermore, the morphology of the β-Mg 17 Al 12 phase in the alloy with addition of 0.3%Sr changes from continuously irregular strip-like shape to discontinuously irregular strip-like shape and/or fine granule-like shape. At the same time, some lamella-like eutectic phases are found in the alloys with additions of 2.5% Sr and 5.0% Sr, and the lamella spacing in the alloy with addition of 5.0% Sr is finer. Adding high Sr content to the AZ31 alloy can bring the new ternary eutectic and/or divorced eutectic phase of Mg 11 Al 5 Zn 4 in the alloy, and the Mg 17 Sr 2 and Mg 2 Sr phases are formed in the alloys with additions of 2.5% Sr and 5.0% Sr.
基金Project(NCET-11-0554)supported by the Program for New Century Excellent Talents in University,ChinaProject(2011BAE22B04)supported by National Key Technology R&D Program of ChinaProject(51271206)supported by the National Natural Science Foundation of China