Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded jo...Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded joints were investigated. The results indicate that the microstructure in the fusion zone is fine, and the microstructure in the heat-affected zone is coarser than the parent metal. The tensile strength of the welded joint is about 84% that of the parent metal. The fracture occurs in a mixed type of toughness and brittleness in the heat-affected zone. During the welding process, aluminum and cerium are enriched at grain boundaries in the fusion zone.展开更多
在803 K LiCl-KCl熔盐中,研究了通过添加助剂AlCl3直接电化学还原Sm2O3和Al-Sm合金的形成。以SmCl3为原料作为参照,采用循环伏安和方波伏安方法,研究了Sm2O3在LiCl-KCl-AlCl3熔盐体系中的电化学行为。通过对比发现在两个体系中,峰的数...在803 K LiCl-KCl熔盐中,研究了通过添加助剂AlCl3直接电化学还原Sm2O3和Al-Sm合金的形成。以SmCl3为原料作为参照,采用循环伏安和方波伏安方法,研究了Sm2O3在LiCl-KCl-AlCl3熔盐体系中的电化学行为。通过对比发现在两个体系中,峰的数量和位置基本一致,这说明在LiCl-KCl熔盐中,加入AlCl3之后,可以将Sm2O3有效氯化。计时电位结果表明,当阴极电流比-139.8 mA.cm-2更负时,Al和Sm共同还原。为了提取Sm,采用恒电流从LiCl-KCl-AlCl3-Sm2O3熔盐中电解得到Al-Sm合金样品,并进行XRD表征,结果表明可以通过调节AlCl3和Sm2O3的浓度得到不同相的Al-Sm合金。展开更多
基金Project (51001034) supported by the National Natural Science Foundation of ChinaProject (208181) supported by the Key Project of Chinese Ministry of Education+1 种基金Projects (2008AA4CH044, 2009AA1AG065, 2010AA4BE031) supported by the Key Project of Science and Technology of Harbin City, ChinaProject (HEUCF101001) supported by the Fundamental Research Funds for the Central Universities, China
文摘Tungsten inert gas weld was carried out on super-light magnesium-lithium alloy plates with a thickness of 2 mm, using argon gas as a protecting atmosphere. The microstructure and mechanical properties of the welded joints were investigated. The results indicate that the microstructure in the fusion zone is fine, and the microstructure in the heat-affected zone is coarser than the parent metal. The tensile strength of the welded joint is about 84% that of the parent metal. The fracture occurs in a mixed type of toughness and brittleness in the heat-affected zone. During the welding process, aluminum and cerium are enriched at grain boundaries in the fusion zone.
文摘在803 K LiCl-KCl熔盐中,研究了通过添加助剂AlCl3直接电化学还原Sm2O3和Al-Sm合金的形成。以SmCl3为原料作为参照,采用循环伏安和方波伏安方法,研究了Sm2O3在LiCl-KCl-AlCl3熔盐体系中的电化学行为。通过对比发现在两个体系中,峰的数量和位置基本一致,这说明在LiCl-KCl熔盐中,加入AlCl3之后,可以将Sm2O3有效氯化。计时电位结果表明,当阴极电流比-139.8 mA.cm-2更负时,Al和Sm共同还原。为了提取Sm,采用恒电流从LiCl-KCl-AlCl3-Sm2O3熔盐中电解得到Al-Sm合金样品,并进行XRD表征,结果表明可以通过调节AlCl3和Sm2O3的浓度得到不同相的Al-Sm合金。