Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld meta...Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (Ni) to fatigue life to failure(Nf) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin’s model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.展开更多
A non-linear continuum damage model was presented based on the irreversible thermodynamics framework developed by LEMAITRE and CHABOCHE. The proposed model was formulated by taking into account the influence of loadin...A non-linear continuum damage model was presented based on the irreversible thermodynamics framework developed by LEMAITRE and CHABOCHE. The proposed model was formulated by taking into account the influence of loading frequency on fatigue life. The parameters H and c are constants for frequency-independent materials, but functions of cyclic frequency for frequency-dependent materials. In addition, the expression of the model was discussed in detail at different stress ratios （R）. Fatigue test data of AlZnMgCu1.5 aluminium alloy and AMg6N alloy were used to verify the proposed model. The results showed that the model possesses a good ability of predicting fatigue life at different loading frequencies and stress ratios.展开更多
文摘Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (Ni) to fatigue life to failure(Nf) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin’s model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.
文摘A non-linear continuum damage model was presented based on the irreversible thermodynamics framework developed by LEMAITRE and CHABOCHE. The proposed model was formulated by taking into account the influence of loading frequency on fatigue life. The parameters H and c are constants for frequency-independent materials, but functions of cyclic frequency for frequency-dependent materials. In addition, the expression of the model was discussed in detail at different stress ratios （R）. Fatigue test data of AlZnMgCu1.5 aluminium alloy and AMg6N alloy were used to verify the proposed model. The results showed that the model possesses a good ability of predicting fatigue life at different loading frequencies and stress ratios.