Nitrobenzene has been considered as a significant groundwater contaminant due to its wide usage in explosives, insecticides, herbicides, pharmaceuticals and dyes. Nitrobenzene is of environmental concern because of it...Nitrobenzene has been considered as a significant groundwater contaminant due to its wide usage in explosives, insecticides, herbicides, pharmaceuticals and dyes. Nitrobenzene is of environmental concern because of its toxicity. In the presence of zero-valent iron （ZVI）, reduction of the nitro group is the dominant transformation process for nitrobenzene. A series of experiments were carried out to investigate the kinetics of nitrobenzene reduction by ZVI and the effects of pH and ZVI particle size on nitrobenzene removal in groundwater. The results indicated that nitrobenzene could be reduced to aniline by ZVI; the reduction of nitrobenzene by ZVI followed a pseudo first-order kinetics; the observed nitrobenzene reduction rate constant （k obs ） was 0.0006 min^-1 and the half-life of nitrobenzene （t 1/2 ） was 115.5 min; the mass balance achieved 87.5% for nitrobenzene reduction by the 1 mm ZVI particle and the final removal efficiency was 80.98%. In addition, the pH and ZVI particle size were found to exhibit significant influences on the nitrobenzene reduction. The observed nitrobenzene reduction rate constant linearly decreased with increase pH and the data fitted on polynomial regression equation for the observed nitrobenzene reduction rate constant and ZVI particle size. Therefore, use of ZVI based permeable reactive barrier technology to remedy nitrobenzene contaminated groundwater was feasible.展开更多
Although considerable research has been conducted on nitrate reduction by zero-valent iron powder （Fe^0）, these studies were mostly operated under anaerobic conditions with invariable pH that was unsuitable for prac...Although considerable research has been conducted on nitrate reduction by zero-valent iron powder （Fe^0）, these studies were mostly operated under anaerobic conditions with invariable pH that was unsuitable for practical application. Without reaction conditions （dissolved oxygen or reaction pH） control, this work aimed at subjecting the kinetics of denitrification by microscale Fe^0 （160-200 mesh） to analysis the factors affecting the denitrification of nitrate and the composition of iron reductive products coating upon the iron surface. Results of the kinetics study have indicated that a higher initial concentration of nitrate would yield a greater reaction rate constant. The reduction rate of nitrate increased with increasing Fe^0 dosage. The reaction can be described as a pseudo-first order reaction with respect to nitrate concentration or Fe^0 dosage. Experimental results also suggested that nitrate reduction by microscale Fe^0 without reaction condition control primarily was an acid-driven surface-mediated process, and the reaction order was 0.65 with respect to hydrogen ion concentration. The analyses of X-ray diffractometry and X-ray photoelectron spectroscopy indicated that a black coating, consisted of Fe2O3, Fe3O4 and FeO（OH）, was formed on the surface of iron grains as an iron corrosion product when the system initial pH was lower than 5. The proportion of FeO（OH） increased as reaction time went on, whereas the proportion of Fe3O4 decreased.展开更多
基金supported by the National High Technology Research and Development Program(863) of China(No.2007AA06A410)the Water Pollution Control and Management Project(No.2008ZX07207-007-05)the National Natural Science Foundation of China(No.40802055)
文摘Nitrobenzene has been considered as a significant groundwater contaminant due to its wide usage in explosives, insecticides, herbicides, pharmaceuticals and dyes. Nitrobenzene is of environmental concern because of its toxicity. In the presence of zero-valent iron （ZVI）, reduction of the nitro group is the dominant transformation process for nitrobenzene. A series of experiments were carried out to investigate the kinetics of nitrobenzene reduction by ZVI and the effects of pH and ZVI particle size on nitrobenzene removal in groundwater. The results indicated that nitrobenzene could be reduced to aniline by ZVI; the reduction of nitrobenzene by ZVI followed a pseudo first-order kinetics; the observed nitrobenzene reduction rate constant （k obs ） was 0.0006 min^-1 and the half-life of nitrobenzene （t 1/2 ） was 115.5 min; the mass balance achieved 87.5% for nitrobenzene reduction by the 1 mm ZVI particle and the final removal efficiency was 80.98%. In addition, the pH and ZVI particle size were found to exhibit significant influences on the nitrobenzene reduction. The observed nitrobenzene reduction rate constant linearly decreased with increase pH and the data fitted on polynomial regression equation for the observed nitrobenzene reduction rate constant and ZVI particle size. Therefore, use of ZVI based permeable reactive barrier technology to remedy nitrobenzene contaminated groundwater was feasible.
基金supported by the Development Program for Outstanding Young Teachers in Harbin Institute of Technology (No. HITQNJS. 2007. 038)
文摘Although considerable research has been conducted on nitrate reduction by zero-valent iron powder （Fe^0）, these studies were mostly operated under anaerobic conditions with invariable pH that was unsuitable for practical application. Without reaction conditions （dissolved oxygen or reaction pH） control, this work aimed at subjecting the kinetics of denitrification by microscale Fe^0 （160-200 mesh） to analysis the factors affecting the denitrification of nitrate and the composition of iron reductive products coating upon the iron surface. Results of the kinetics study have indicated that a higher initial concentration of nitrate would yield a greater reaction rate constant. The reduction rate of nitrate increased with increasing Fe^0 dosage. The reaction can be described as a pseudo-first order reaction with respect to nitrate concentration or Fe^0 dosage. Experimental results also suggested that nitrate reduction by microscale Fe^0 without reaction condition control primarily was an acid-driven surface-mediated process, and the reaction order was 0.65 with respect to hydrogen ion concentration. The analyses of X-ray diffractometry and X-ray photoelectron spectroscopy indicated that a black coating, consisted of Fe2O3, Fe3O4 and FeO（OH）, was formed on the surface of iron grains as an iron corrosion product when the system initial pH was lower than 5. The proportion of FeO（OH） increased as reaction time went on, whereas the proportion of Fe3O4 decreased.