The processing of high strength Al wrought alloys does lead either to restrictions for geometrical complexity or to high production costs due to low productivity and multiple-step processes. Thixoextrusion process to ...The processing of high strength Al wrought alloys does lead either to restrictions for geometrical complexity or to high production costs due to low productivity and multiple-step processes. Thixoextrusion process to overcome these difficulties has been under investigation. In the present study, the effect of thixoextrusion parameters was investigated on mechanical properties of 7003 Al wrought alloy. The maximum extrusion pressure of the thixoextrusion process is three times lower than that of the hot extrusion process. The elongated grains which have the axisymmetry with extrusion direction are generally observed during hot extrusion process, while the microstructures of the thixoextruded are isotropic. The tensile and yield strengthes of the thixoextruded bar are lower than those of the hot extruded bar, while the elongation value of the thixoextruded bar is higher than that of the hot extruded bar.展开更多
Cold-rolling workability, heat treatment characteristics and mechanical properties of Mg-5%-22%Li-2%Zn(mass fraction) wrought alloys were studied. Density of alloys is between 1.19 and 1.62 g/cm^3. The limit of reduct...Cold-rolling workability, heat treatment characteristics and mechanical properties of Mg-5%-22%Li-2%Zn(mass fraction) wrought alloys were studied. Density of alloys is between 1.19 and 1.62 g/cm^3. The limit of reduction for cold rolling of the β phase alloys at 16% and 22%Li exceeds 90% at room temperature. The properties and microstructures of Mg-Li-Zn alloys were studied, which were homogenized, cold rolled, then annealed at different temperatures. Recrystallization behaviors of the alloys were investigated through microstructures observing and hardness measuring. The results show that the cast billets are suitable for rolling after homogenization at 573K for 12 h for Mg-9Li-2Zn-2Ca alloy and at 523K for 24 h for Mg-9Li-2Zn-2Ca alloy. The cold rolled plates were completely recrystallizated by annealing at 573K for 1 h.展开更多
文摘The processing of high strength Al wrought alloys does lead either to restrictions for geometrical complexity or to high production costs due to low productivity and multiple-step processes. Thixoextrusion process to overcome these difficulties has been under investigation. In the present study, the effect of thixoextrusion parameters was investigated on mechanical properties of 7003 Al wrought alloy. The maximum extrusion pressure of the thixoextrusion process is three times lower than that of the hot extrusion process. The elongated grains which have the axisymmetry with extrusion direction are generally observed during hot extrusion process, while the microstructures of the thixoextruded are isotropic. The tensile and yield strengthes of the thixoextruded bar are lower than those of the hot extruded bar, while the elongation value of the thixoextruded bar is higher than that of the hot extruded bar.
基金Project supported by National High Tech Research Programof China (2001AA335010)
文摘Cold-rolling workability, heat treatment characteristics and mechanical properties of Mg-5%-22%Li-2%Zn(mass fraction) wrought alloys were studied. Density of alloys is between 1.19 and 1.62 g/cm^3. The limit of reduction for cold rolling of the β phase alloys at 16% and 22%Li exceeds 90% at room temperature. The properties and microstructures of Mg-Li-Zn alloys were studied, which were homogenized, cold rolled, then annealed at different temperatures. Recrystallization behaviors of the alloys were investigated through microstructures observing and hardness measuring. The results show that the cast billets are suitable for rolling after homogenization at 573K for 12 h for Mg-9Li-2Zn-2Ca alloy and at 523K for 24 h for Mg-9Li-2Zn-2Ca alloy. The cold rolled plates were completely recrystallizated by annealing at 573K for 1 h.