对DP590双相钢点焊接头进行正交试验,研究不同工艺因素对点焊接头失效载荷和焊核直径的影响,确定最优点焊工艺参数,并探讨点焊接头压痕深度的超声测量方法.采用超声波水浸聚焦入射法对1.5 mm厚的DP590双相钢点焊接头进行超声C扫描,获得...对DP590双相钢点焊接头进行正交试验,研究不同工艺因素对点焊接头失效载荷和焊核直径的影响,确定最优点焊工艺参数,并探讨点焊接头压痕深度的超声测量方法.采用超声波水浸聚焦入射法对1.5 mm厚的DP590双相钢点焊接头进行超声C扫描,获得接头焊核直径,利用超声A扫信号,计算点焊接头压痕深度,并与实际测量结果对比.研究表明:焊接参数对DP590点焊接头的失效载荷与焊核直径的显著性影响一致,从大到小依次为焊接电流、焊接时间、电极压力;DP590点焊接头最优的焊接工艺参数为:焊接时间70 ms,焊接电流15.0 k A,电极压力6.5 k N,在此参数下接头的抗拉强度为9 521.4 N;超声A扫信号计算得到的点焊接头表面压痕率与实际压痕率的误差在2.5%~9.7%,超声计算所得压痕深度与实际测量压痕率较为接近.展开更多
The impact wear behavior and damage mechanism of dissimilar welded joints between U26Mn frog and U75 V rail before and after normalizing treatment were studied by cyclic impact tests.The experiment indicated that the ...The impact wear behavior and damage mechanism of dissimilar welded joints between U26Mn frog and U75 V rail before and after normalizing treatment were studied by cyclic impact tests.The experiment indicated that the impact wear volume of the joints increased with the increasing number of impact cycles.The main wear mechanisms include pitting wear,mild fatigue wear,delamination wear,and fatigue wear,and plastic deformation was the primary impact wear mechanism.Among them,fatigue wear had the greatest influence on wear volume,while other wear mechanisms had limited effect.The impact wear resistance of the base material was better than that of the heat-affected zone.Normalizing treatment was beneficial to improving the impact wear resistance of welded joints owing to its effect to promote pearlite recovery,grain refinement,and uniform distribution of grains.The martensite generated in the rail welded joints aggravated the impact wear damage to the materials,which should be avoided.展开更多
Based on a large amount of dissection at welded interface and quantitative microscopic examination of welded rate, the suitable limit grey scale value was determined, and the welded rate of superplastic solid state w...Based on a large amount of dissection at welded interface and quantitative microscopic examination of welded rate, the suitable limit grey scale value was determined, and the welded rate of superplastic solid state welding interface of heterogeneous steel was systematically studied by means of self made ultrasonic C scanning imaging inspection system. The experimental results show: the welded state of superplastic solid state welding interface of heterogeneous steel can be conducted to be more accurately, reliably and quickly inspected by means of this system, and the ultrasonic testing results are good consistent with actual examination results of the interface defective distribution. Within the extent of the suitble welded rate,the welded rate in 40Cr/T10A superplastic welding process tested by this system is linear with its tensile strength of joint.展开更多
In welding, so many factors contribute to good quality welds. The deposition rate is the rate of weld metal deposit at fusion zone during welding, which also is a key factors affecting the quality of welded joints. To...In welding, so many factors contribute to good quality welds. The deposition rate is the rate of weld metal deposit at fusion zone during welding, which also is a key factors affecting the quality of welded joints. Too high or low deposition rate compromises the integrity of weld. This study was carried out with the aim of providing an approach for producing better weldments by optimizing and predicting deposition rate of low carbon steel using Response Surface Methodology (RSM). 30 sets of experiments were done, adopting the central composite experimental design. The tungsten inert gas welding equipment was used to produce the welded joints. Argon gas was supplied to the welding process to shield the weld from atmospheric interference. Mild steel coupons measuring 60 × 40 × 10 mm was used for the experiments. The results obtained show that the voltage and current have very strong influence on the deposition rate. The models developed possess a variance inflation factor of 1. And P-value is less than 0.05, indicating that the model is significant. The models also possessed a high goodness of fit with R2 (Coefficient of determination) values of 91%. The model produced numerically obtained optimal solution of current of 160.00 Amp, voltage of 20 volts and a gas flow rate of 17 L/min produces a welded material having deposition rate of 0.4637 kg/hr. This solution was selected by design expert as the optimal solution with a desirability value of 98.8%. A weld simulation using the optimum value obtained produced a weld with good quality.展开更多
文摘对DP590双相钢点焊接头进行正交试验,研究不同工艺因素对点焊接头失效载荷和焊核直径的影响,确定最优点焊工艺参数,并探讨点焊接头压痕深度的超声测量方法.采用超声波水浸聚焦入射法对1.5 mm厚的DP590双相钢点焊接头进行超声C扫描,获得接头焊核直径,利用超声A扫信号,计算点焊接头压痕深度,并与实际测量结果对比.研究表明:焊接参数对DP590点焊接头的失效载荷与焊核直径的显著性影响一致,从大到小依次为焊接电流、焊接时间、电极压力;DP590点焊接头最优的焊接工艺参数为:焊接时间70 ms,焊接电流15.0 k A,电极压力6.5 k N,在此参数下接头的抗拉强度为9 521.4 N;超声A扫信号计算得到的点焊接头表面压痕率与实际压痕率的误差在2.5%~9.7%,超声计算所得压痕深度与实际测量压痕率较为接近.
基金The work was supported by the National Key Research and Development Project(2017YFB0304500).
文摘The impact wear behavior and damage mechanism of dissimilar welded joints between U26Mn frog and U75 V rail before and after normalizing treatment were studied by cyclic impact tests.The experiment indicated that the impact wear volume of the joints increased with the increasing number of impact cycles.The main wear mechanisms include pitting wear,mild fatigue wear,delamination wear,and fatigue wear,and plastic deformation was the primary impact wear mechanism.Among them,fatigue wear had the greatest influence on wear volume,while other wear mechanisms had limited effect.The impact wear resistance of the base material was better than that of the heat-affected zone.Normalizing treatment was beneficial to improving the impact wear resistance of welded joints owing to its effect to promote pearlite recovery,grain refinement,and uniform distribution of grains.The martensite generated in the rail welded joints aggravated the impact wear damage to the materials,which should be avoided.
基金supported by Henan Natural Science Foundation of China under Grant No:984040900
文摘Based on a large amount of dissection at welded interface and quantitative microscopic examination of welded rate, the suitable limit grey scale value was determined, and the welded rate of superplastic solid state welding interface of heterogeneous steel was systematically studied by means of self made ultrasonic C scanning imaging inspection system. The experimental results show: the welded state of superplastic solid state welding interface of heterogeneous steel can be conducted to be more accurately, reliably and quickly inspected by means of this system, and the ultrasonic testing results are good consistent with actual examination results of the interface defective distribution. Within the extent of the suitble welded rate,the welded rate in 40Cr/T10A superplastic welding process tested by this system is linear with its tensile strength of joint.
文摘In welding, so many factors contribute to good quality welds. The deposition rate is the rate of weld metal deposit at fusion zone during welding, which also is a key factors affecting the quality of welded joints. Too high or low deposition rate compromises the integrity of weld. This study was carried out with the aim of providing an approach for producing better weldments by optimizing and predicting deposition rate of low carbon steel using Response Surface Methodology (RSM). 30 sets of experiments were done, adopting the central composite experimental design. The tungsten inert gas welding equipment was used to produce the welded joints. Argon gas was supplied to the welding process to shield the weld from atmospheric interference. Mild steel coupons measuring 60 × 40 × 10 mm was used for the experiments. The results obtained show that the voltage and current have very strong influence on the deposition rate. The models developed possess a variance inflation factor of 1. And P-value is less than 0.05, indicating that the model is significant. The models also possessed a high goodness of fit with R2 (Coefficient of determination) values of 91%. The model produced numerically obtained optimal solution of current of 160.00 Amp, voltage of 20 volts and a gas flow rate of 17 L/min produces a welded material having deposition rate of 0.4637 kg/hr. This solution was selected by design expert as the optimal solution with a desirability value of 98.8%. A weld simulation using the optimum value obtained produced a weld with good quality.