A high-manganese austenitic steel matrix （Mn13） composite reinforced with TiN ceramic particles was synthesized by means of Vacuum-Evaporation Pattern Casting （V-EPC）. The composite microstructure and interface bo...A high-manganese austenitic steel matrix （Mn13） composite reinforced with TiN ceramic particles was synthesized by means of Vacuum-Evaporation Pattern Casting （V-EPC）. The composite microstructure and interface bonding of TiN/matrix were analyzed utilizing optical microscope （OM） and X-ray diffraction （XRD）. The effects of different volume fraction of TiN on impact wear resistance were evaluated by MLD-10 impact wear test. The results showed that TiN was evenly distributed in composite layer and had a good interface bonding with matrix when the volume fractions of TiN were 27% and 36% respectively. However, cast defects and TiN agglomeration occurred when the TiN volume fraction increased to 48~. Compared with high-manganese austenitic steel （Mnl3）, the im- pact wear resistance of the TiN-reinforced composite is better. In small impact load conditions, composite layer can effectively resist abrasives wear and TiN particles played an important role in determining impact wear resistance of composite layer. In large impact load, the synergistic roles of spalling of TiN particles and the increase of work hardening of Mn13 based material are responsible for impact wear resistance.展开更多
The effects of laser shock peening (LSP) on the impact wear behavior of Ti-6Al-4V alloys were investigated by a homemade impact wear test rig. The microstructure and mechanical properties of the peened samples were st...The effects of laser shock peening (LSP) on the impact wear behavior of Ti-6Al-4V alloys were investigated by a homemade impact wear test rig. The microstructure and mechanical properties of the peened samples were studied. During the impact wear test, the energy absorption, impact force, wear contact time and wear mechanism of all the test samples were investigated in terms of the influence of the impact kinetic energy. The results showed that microhardness, elastic modulus and residual compressive stress of the treated samples were markedly improved. The wear resistances of both treated samples were highly improved after LSP, and a higher pulse energy corresponded to a more obvious effect. Besides, the wear in all test samples involved a combination of abrasive and oxidation wear and fatigue spalling.展开更多
A great amount of iron grinding balls in tube mills have been consumed. Under this impact abrasive wear working condition, the failure of wear resistant alloying white irons grinding balls is mainly caused by fatigue ...A great amount of iron grinding balls in tube mills have been consumed. Under this impact abrasive wear working condition, the failure of wear resistant alloying white irons grinding balls is mainly caused by fatigue spalling. The impact wear resistance of martensitic high chromium cast iron （Cr of 15%） is not high sometimes, but its cost is not low. Thus, medium Cr-Si wear resistant cast iron is recommended. The influence of the iron on impact fatigue resistance and impact wear resistance is pronounced. Ball-on-ball impact fatigue test and high stress impact wear test of the grinding balls have been carried out. The results show that the impact fatigue resistance （IFR） and impact wear resistance （IWR） of medium Cr-Si cast iron are superior to those of martensitic high chromium cast iron （Cr of 15%）. The main reasons are that （1） the stress in medium Cr-Si cast iron is released in the as-cast state; （2） the matrix is fine pearlite with better toughness and plasticity; （3） the pearlite is more stable compared with a retained austenite under repeated impact load and less phase transformation can take place; （4） high silicon content im- proves the morphology of eutectic carbide; （5） there is no seeondary carbide which results in less crack sources. All these factors are beneficial to improvement of impact fatigue spalling resistance. The eutectic carbide M7C3 is the main constituent to resist wear.展开更多
利用高分辨透射电子显微镜和原子力显微镜观察了含纳米颗粒溶液冲蚀硅片表面损伤行为,考察了纳米颗粒碰撞单晶硅片所导致的微观物理损伤.结果表明:冲蚀30 s后,在高分辨透射电子显微镜下可见硅片表面呈现方向性损伤,并可观察到大量非均...利用高分辨透射电子显微镜和原子力显微镜观察了含纳米颗粒溶液冲蚀硅片表面损伤行为,考察了纳米颗粒碰撞单晶硅片所导致的微观物理损伤.结果表明:冲蚀30 s后,在高分辨透射电子显微镜下可见硅片表面呈现方向性损伤,并可观察到大量非均匀的晶格缺陷;当冲蚀10 m in时,硅片表面出现微观划痕和凹坑,在划痕一端可见原子堆积,亚表面可观察到镶嵌晶粒的非晶损伤层;继续延长冲蚀时间将加剧其表面损伤.展开更多
基金Item Sponsored by Office of Education of Shaanxi Province of China(08JK345)Programs for Industry Development of Shaanxi Province of China(2008K06-18)
文摘A high-manganese austenitic steel matrix （Mn13） composite reinforced with TiN ceramic particles was synthesized by means of Vacuum-Evaporation Pattern Casting （V-EPC）. The composite microstructure and interface bonding of TiN/matrix were analyzed utilizing optical microscope （OM） and X-ray diffraction （XRD）. The effects of different volume fraction of TiN on impact wear resistance were evaluated by MLD-10 impact wear test. The results showed that TiN was evenly distributed in composite layer and had a good interface bonding with matrix when the volume fractions of TiN were 27% and 36% respectively. However, cast defects and TiN agglomeration occurred when the TiN volume fraction increased to 48~. Compared with high-manganese austenitic steel （Mnl3）, the im- pact wear resistance of the TiN-reinforced composite is better. In small impact load conditions, composite layer can effectively resist abrasives wear and TiN particles played an important role in determining impact wear resistance of composite layer. In large impact load, the synergistic roles of spalling of TiN particles and the increase of work hardening of Mn13 based material are responsible for impact wear resistance.
基金Project(2016YFB1102601)supported by the National Key R&D Program of ChinaProjects(51375407,U1530136)supported by the National Natural Science Foundation of ChinaProject(2017TD0017)supported by the Young Scientific Innovation Team of Science and Technology of Sichuan Province,China
文摘The effects of laser shock peening (LSP) on the impact wear behavior of Ti-6Al-4V alloys were investigated by a homemade impact wear test rig. The microstructure and mechanical properties of the peened samples were studied. During the impact wear test, the energy absorption, impact force, wear contact time and wear mechanism of all the test samples were investigated in terms of the influence of the impact kinetic energy. The results showed that microhardness, elastic modulus and residual compressive stress of the treated samples were markedly improved. The wear resistances of both treated samples were highly improved after LSP, and a higher pulse energy corresponded to a more obvious effect. Besides, the wear in all test samples involved a combination of abrasive and oxidation wear and fatigue spalling.
基金Item Sponsored by Foundation of China National Nonferrous Metals Industry Corporation(96-124)
文摘A great amount of iron grinding balls in tube mills have been consumed. Under this impact abrasive wear working condition, the failure of wear resistant alloying white irons grinding balls is mainly caused by fatigue spalling. The impact wear resistance of martensitic high chromium cast iron （Cr of 15%） is not high sometimes, but its cost is not low. Thus, medium Cr-Si wear resistant cast iron is recommended. The influence of the iron on impact fatigue resistance and impact wear resistance is pronounced. Ball-on-ball impact fatigue test and high stress impact wear test of the grinding balls have been carried out. The results show that the impact fatigue resistance （IFR） and impact wear resistance （IWR） of medium Cr-Si cast iron are superior to those of martensitic high chromium cast iron （Cr of 15%）. The main reasons are that （1） the stress in medium Cr-Si cast iron is released in the as-cast state; （2） the matrix is fine pearlite with better toughness and plasticity; （3） the pearlite is more stable compared with a retained austenite under repeated impact load and less phase transformation can take place; （4） high silicon content im- proves the morphology of eutectic carbide; （5） there is no seeondary carbide which results in less crack sources. All these factors are beneficial to improvement of impact fatigue spalling resistance. The eutectic carbide M7C3 is the main constituent to resist wear.
文摘利用高分辨透射电子显微镜和原子力显微镜观察了含纳米颗粒溶液冲蚀硅片表面损伤行为,考察了纳米颗粒碰撞单晶硅片所导致的微观物理损伤.结果表明:冲蚀30 s后,在高分辨透射电子显微镜下可见硅片表面呈现方向性损伤,并可观察到大量非均匀的晶格缺陷;当冲蚀10 m in时,硅片表面出现微观划痕和凹坑,在划痕一端可见原子堆积,亚表面可观察到镶嵌晶粒的非晶损伤层;继续延长冲蚀时间将加剧其表面损伤.