Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures ...Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.展开更多
This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene sphe...This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure inter- connection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexde- cyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.展开更多
The catalytic performances of monolithic catalyst Ru/Al2O3/Cordierite in selective hydrogenation of benzene to cyclohexene were examined in a circulated monolithic fix-bed reactor.The monolithic catalyst exhibited exc...The catalytic performances of monolithic catalyst Ru/Al2O3/Cordierite in selective hydrogenation of benzene to cyclohexene were examined in a circulated monolithic fix-bed reactor.The monolithic catalyst exhibited excellent performances in the selective hydrogenation of benzene to cyclohexene;a high cyclohexene yield of 18% was obtained.The addition of aqueous solution of ZnSO4 during reaction was important to obtain high cyclohexene selectivity.The results indicated that both the catalyst with high activity and selectivity and the intensification of external diffusion for cyclohexene were crucial to get high cyclohexene yield.展开更多
The noble metals (Pt, Pd, Rh) supported on Cu-Ce mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate were investigated as catalytic performance of Three Way Catalysts (TWC) under simulated automotive exhaust feed gas...The noble metals (Pt, Pd, Rh) supported on Cu-Ce mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate were investigated as catalytic performance of Three Way Catalysts (TWC) under simulated automotive exhaust feed gas. The structural, morphological features and catalytic activity were observed by X-ray diffractometry (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS) and GC-TCD (Varian CP-4900). The catalytic performance of noble metals (Pt, Rh, Pd) supported on Cu-Ce mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate was be compared with noble metals (Pt, Rh, Pd) supported on Ce-Zr mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate and only γ-Al2O3 washcoat/FeCrAl substrate at various stoichiometric ratio of oxygen. The results showed that the addition of Cu-Ce mixed oxides improved CO oxidation reaction at lower temperature during stable lambda of 1, the highest CO conversion of 99% is observed for the noble metals (Pt, Pd, Rh) support on Cu-Ce with γ-Al2O3 washcoat/FeCrAl substrate. The results also showed that, the addition of Cu-Ce mixed oxides promoted released oxygen, thus it improved strongly CO and C3H8 conversion at lean oxygen stoichiometric operation.展开更多
This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene sphe...This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure interconnection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexdecyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.展开更多
基金[The work was financially supported by the National Key Basic Research Program of China ("973")(No. 2004CB719503).]
文摘Ce-Zr compounds such as Cc0.68Zr0.3202 solid solution, Ce/Zr nitrate and CeO2/ZrO2 were added into γ-alumina-based slurries, which were then loaded on FeCrAl foils pretreated at 950℃ and 1100℃. The microstructures and adhesion performance between the substrates and the washcoats were measured by SEM, BET surface area, ultrasonic vibration and thermal shock test. The results show that the addition of Ce0.68Zr0.32O2 solid solution, Ce/Zr nitrate and CeO2/ZrO2 into the slurries can improve γ-Al2O3-based washcoat adhesion on FeCrAl foils. Furthermore, ceria-zirconia solid solution increases the adhesion of the washcoat on the surface of an FeCrAl foil than the two others. The specific surface area of this washcoat remains about 4345 m^2/g and the weight loss is below 4.0% even after aging test of 10% steam-containing air at 1050℃ for 20 h.
基金NUFFIC, CSC and the Scientific Research Fund of Hunan Provincial Education Department (No.04B060).
文摘This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure inter- connection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexde- cyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.
文摘The catalytic performances of monolithic catalyst Ru/Al2O3/Cordierite in selective hydrogenation of benzene to cyclohexene were examined in a circulated monolithic fix-bed reactor.The monolithic catalyst exhibited excellent performances in the selective hydrogenation of benzene to cyclohexene;a high cyclohexene yield of 18% was obtained.The addition of aqueous solution of ZnSO4 during reaction was important to obtain high cyclohexene selectivity.The results indicated that both the catalyst with high activity and selectivity and the intensification of external diffusion for cyclohexene were crucial to get high cyclohexene yield.
文摘The noble metals (Pt, Pd, Rh) supported on Cu-Ce mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate were investigated as catalytic performance of Three Way Catalysts (TWC) under simulated automotive exhaust feed gas. The structural, morphological features and catalytic activity were observed by X-ray diffractometry (XRD), scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS) and GC-TCD (Varian CP-4900). The catalytic performance of noble metals (Pt, Rh, Pd) supported on Cu-Ce mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate was be compared with noble metals (Pt, Rh, Pd) supported on Ce-Zr mixed oxides with γ-Al2O3 washcoat/FeCrAl substrate and only γ-Al2O3 washcoat/FeCrAl substrate at various stoichiometric ratio of oxygen. The results showed that the addition of Cu-Ce mixed oxides improved CO oxidation reaction at lower temperature during stable lambda of 1, the highest CO conversion of 99% is observed for the noble metals (Pt, Pd, Rh) support on Cu-Ce with γ-Al2O3 washcoat/FeCrAl substrate. The results also showed that, the addition of Cu-Ce mixed oxides promoted released oxygen, thus it improved strongly CO and C3H8 conversion at lean oxygen stoichiometric operation.
文摘This paper reports how a hairy layer of carbon nano-fibers can be prepared on the macro-porous silica foam produced by the sphere templating method. Firstly, three-dimensional close-packed crystals of polystyrene spheres are assembled on porous disk substrate by vacuum filtration or evaporation. The polystyrene template is annealed slightly above the glass transition temperature in order to strengthen the colloidal crystal and ensure interconnection of the spheres so as to obtain porous materials with open structure. Following the treatment of hexdecyltrimethylammonium bromide, the polystyrene template is filled with silica colloidal solution, which solidifies in the cavities. Then the polystyrene particles are removed by calcination at 843K, leaving behind porous silica foam. Scanning electron microscopy images demonstrate that silica foam has uniform and open structured pores. Nickel particles were deposited on porous silica foam layer by the dipping method and porous carbon nano-fiber washcoat was prepared by catalytic decomposition of ethene over small nickel particles.