纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能...纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与展开更多
Nano-silica treated with different kinds of coupling agent （KH550, A-143, A-151） was used to modify the surface condition of glass fiber, and then, the modified glass fiber/unsaturated polyester resin （UPR） compos...Nano-silica treated with different kinds of coupling agent （KH550, A-143, A-151） was used to modify the surface condition of glass fiber, and then, the modified glass fiber/unsaturated polyester resin （UPR） composites materials were prepared. Scanning electron microscopy （SEM）, dynamic mechanical analysis （DMA）, and impact test were used to characterize the composite materials＇ structure and properties. The morphology of composite materials shows that the adhesion between nano-silica and glass fiber is improved when silane coupling agent is added in. The DMA and impact test results show that silane coupling agent （especially KH550 and A-151） could effectively improve the composite＇s mechanical properties. When the dose of KH550 was 0.1% （m ： m）, the storage modulus and impact strength reached the maximum.展开更多
文摘纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与
基金Supported by the National Natural Science Foundation of of China(J1210061)
文摘Nano-silica treated with different kinds of coupling agent （KH550, A-143, A-151） was used to modify the surface condition of glass fiber, and then, the modified glass fiber/unsaturated polyester resin （UPR） composites materials were prepared. Scanning electron microscopy （SEM）, dynamic mechanical analysis （DMA）, and impact test were used to characterize the composite materials＇ structure and properties. The morphology of composite materials shows that the adhesion between nano-silica and glass fiber is improved when silane coupling agent is added in. The DMA and impact test results show that silane coupling agent （especially KH550 and A-151） could effectively improve the composite＇s mechanical properties. When the dose of KH550 was 0.1% （m ： m）, the storage modulus and impact strength reached the maximum.