150 cm wide AZ31 magnesium alloy sheet was produced by twin roll casting.The sheets of 6 mm thickness were cast. The sheet material was characterized using various techniques including metallography and XRD.The mechan...150 cm wide AZ31 magnesium alloy sheet was produced by twin roll casting.The sheets of 6 mm thickness were cast. The sheet material was characterized using various techniques including metallography and XRD.The mechanical properties were investigated by tensile tests and hardness measurements.The procedures were developed for thermomechanical treatment of cast sheet material.The products of these procedures were characterized and the results were discussed for possible potential applications.展开更多
The twin roll caster for aluminum alloys has many a dv antages. For example, rapid solidification, low equipment cost, and low running cost, etc. However, the twin roll caster has some disadvantages. They are slow c a...The twin roll caster for aluminum alloys has many a dv antages. For example, rapid solidification, low equipment cost, and low running cost, etc. However, the twin roll caster has some disadvantages. They are slow c asting speed and limitation of alloys. In the conventional twin roll caster, the casting speed is slower than 10 m/min. Aluminum alloys, which freezing range is wide, can not be cast. In the present study, break through of these problems wa s tried, and a new type twin roll caster was devised. A vertical type twin roll caster equipped with a nozzle was devised in order to cast aluminum strips at the speeds higher than 60 m/min. Characteristic features of this caster were vertical type, use of copper rolls, low separating force (n o operation of rolling), no use of lubricant, and equipment of the nozzle. In th e high speed roll casting, feed of molten metal of the vertical type twin roll c aster was easier than that of the conventional horizontal type caster. The use o f the copper rolls made cooling rate higher. The low separating force and the us e of the copper rolls prevented sticking of the strip to the roll. The lubricant was not needed, as the sticking of the strip to the roll did not occur. No use of the lubricant was useful to increase the cooling rate and casting speed of th e strip. The nozzle was used in order to improve contact condition (heat transfe r) between the melt and the rolls by hydrostatic pressure. In the twin roll cast er of the present study, many devices were done to improve the cooling condition of the strip in order to increase the casting speed. It was said that the roll casting of A5182 was very difficult, as freezing zone of A5182 was very wide. However, A5182 strip could be cast at high speeds up to 120 m/min using the twin roll caster of the present study. The microstructure of the strip cast using the conventional type twin roll caster is columnar structu re. The microstructure of the strip cast using the twin roll caster of the prese nt study was not columnar but equ展开更多
文摘150 cm wide AZ31 magnesium alloy sheet was produced by twin roll casting.The sheets of 6 mm thickness were cast. The sheet material was characterized using various techniques including metallography and XRD.The mechanical properties were investigated by tensile tests and hardness measurements.The procedures were developed for thermomechanical treatment of cast sheet material.The products of these procedures were characterized and the results were discussed for possible potential applications.
文摘The twin roll caster for aluminum alloys has many a dv antages. For example, rapid solidification, low equipment cost, and low running cost, etc. However, the twin roll caster has some disadvantages. They are slow c asting speed and limitation of alloys. In the conventional twin roll caster, the casting speed is slower than 10 m/min. Aluminum alloys, which freezing range is wide, can not be cast. In the present study, break through of these problems wa s tried, and a new type twin roll caster was devised. A vertical type twin roll caster equipped with a nozzle was devised in order to cast aluminum strips at the speeds higher than 60 m/min. Characteristic features of this caster were vertical type, use of copper rolls, low separating force (n o operation of rolling), no use of lubricant, and equipment of the nozzle. In th e high speed roll casting, feed of molten metal of the vertical type twin roll c aster was easier than that of the conventional horizontal type caster. The use o f the copper rolls made cooling rate higher. The low separating force and the us e of the copper rolls prevented sticking of the strip to the roll. The lubricant was not needed, as the sticking of the strip to the roll did not occur. No use of the lubricant was useful to increase the cooling rate and casting speed of th e strip. The nozzle was used in order to improve contact condition (heat transfe r) between the melt and the rolls by hydrostatic pressure. In the twin roll cast er of the present study, many devices were done to improve the cooling condition of the strip in order to increase the casting speed. It was said that the roll casting of A5182 was very difficult, as freezing zone of A5182 was very wide. However, A5182 strip could be cast at high speeds up to 120 m/min using the twin roll caster of the present study. The microstructure of the strip cast using the conventional type twin roll caster is columnar structu re. The microstructure of the strip cast using the twin roll caster of the prese nt study was not columnar but equ
