Due to their high specific strength and low density, magnesium alloys are widely used in many weight-saving applications. This research is aimed at investigating the microstructure and hardness of commercial AZ63 allo...Due to their high specific strength and low density, magnesium alloys are widely used in many weight-saving applications. This research is aimed at investigating the microstructure and hardness of commercial AZ63 alloy specimens subjected to two different thermomechanical treatments （TMTs）. For the first TMT, after solution treated at the temperature of 380 ℃ for 20 h, AZ63 alloy specimens were 5% cold worked by rolling process followed by ageing at the temperatures of 150 ℃and 250 ℃ for 3, 9 and 25 h. In the second TMT, the specimens were solution treated at the temperature of 380 ℃ for 20 h, underwent 2% cold worked and quenched in water of 0 ℃. Half of the specimens were then 2% cold worked whilst the rest were rolled to 8% cold worked. All the specimens were then aged at the temperatures of 150 ℃ and 250 ℃ for 3, 9 and 25 h. Optical microscope was used to analyze the microstructures of the specimens. Hardness test was too conducted to measure the effect of the treatments on the specimens. Results show that two-step aging enhances the hardness of the specimens due to the distribution of fine β-phase （MglTA112） in the alloy matrix. The results also reveal that, the best hardness from the first TMT was produced by specimen that was pre-aged at 150 ℃ whereas, in the second TMT, aging at 250 ℃ exhibited the best hardness values.展开更多
Combining with the low temperature material properties and the boiling heat transfer coefficient of specimen immersed in the liquid nitrogen, a numerical model based on metallo-thermo-mechanical couple theory was esta...Combining with the low temperature material properties and the boiling heat transfer coefficient of specimen immersed in the liquid nitrogen, a numerical model based on metallo-thermo-mechanical couple theory was established to reproduce the deep cryogenic treatment （DCT） process of a newly developed cold work die steel Cr8Mo2SiV （SDC99）. Moreover, an experimental setup for rapid temperature measurement was designed to validate the simulation results. The investigation suggests that the differences in temperature and cooling rate between the surface and core of specimen are very significant. However, it should be emphasized that the acute temperature and cooling rate changes during DCT are mainly concentrated on the specimen surface region about 1/3 of the sample thickness. Subjected to DCT, the retained austenite of quenched specimen continues to transform to martensite and finally its phase volume fraction reduces to 2.3%. The predicted results are coincident well with the experimental data, which demonstrates that the numerical model employed in this study can accurately capture the variation characteristics of temperature and microstructure fields during DCT and provide a theoretical guidance for making the reasonable DCT procedure.展开更多
文摘Due to their high specific strength and low density, magnesium alloys are widely used in many weight-saving applications. This research is aimed at investigating the microstructure and hardness of commercial AZ63 alloy specimens subjected to two different thermomechanical treatments （TMTs）. For the first TMT, after solution treated at the temperature of 380 ℃ for 20 h, AZ63 alloy specimens were 5% cold worked by rolling process followed by ageing at the temperatures of 150 ℃and 250 ℃ for 3, 9 and 25 h. In the second TMT, the specimens were solution treated at the temperature of 380 ℃ for 20 h, underwent 2% cold worked and quenched in water of 0 ℃. Half of the specimens were then 2% cold worked whilst the rest were rolled to 8% cold worked. All the specimens were then aged at the temperatures of 150 ℃ and 250 ℃ for 3, 9 and 25 h. Optical microscope was used to analyze the microstructures of the specimens. Hardness test was too conducted to measure the effect of the treatments on the specimens. Results show that two-step aging enhances the hardness of the specimens due to the distribution of fine β-phase （MglTA112） in the alloy matrix. The results also reveal that, the best hardness from the first TMT was produced by specimen that was pre-aged at 150 ℃ whereas, in the second TMT, aging at 250 ℃ exhibited the best hardness values.
基金Project (51171104) supported by the National Natural Science Foundation of China
文摘Combining with the low temperature material properties and the boiling heat transfer coefficient of specimen immersed in the liquid nitrogen, a numerical model based on metallo-thermo-mechanical couple theory was established to reproduce the deep cryogenic treatment （DCT） process of a newly developed cold work die steel Cr8Mo2SiV （SDC99）. Moreover, an experimental setup for rapid temperature measurement was designed to validate the simulation results. The investigation suggests that the differences in temperature and cooling rate between the surface and core of specimen are very significant. However, it should be emphasized that the acute temperature and cooling rate changes during DCT are mainly concentrated on the specimen surface region about 1/3 of the sample thickness. Subjected to DCT, the retained austenite of quenched specimen continues to transform to martensite and finally its phase volume fraction reduces to 2.3%. The predicted results are coincident well with the experimental data, which demonstrates that the numerical model employed in this study can accurately capture the variation characteristics of temperature and microstructure fields during DCT and provide a theoretical guidance for making the reasonable DCT procedure.