Two novel washcoats Ce0.8Zr0.15La0.05Oδ and Ce0.8Zr0.2O2 was prepared by an impregnation method, which acted as a host for the active Pd component to prepare Pd/Ce0.8Zr0.15La0.05Oδ/substrate and Pd/Ce0.8Zr0.2O2/subs...Two novel washcoats Ce0.8Zr0.15La0.05Oδ and Ce0.8Zr0.2O2 was prepared by an impregnation method, which acted as a host for the active Pd component to prepare Pd/Ce0.8Zr0.15La0.05Oδ/substrate and Pd/Ce0.8Zr0.2O2/substrate monolithic catalysts for toluene combustion. The washcoats was characterized by X-ray diffraction (XRD), Raman spectroscopy, Brunauner-Emmett-Teller (BET), and H2-temperature-programmed reduction (H2-TPR). The result indicated that both the washcoats had strong vibration-shock resistance according to ultrasonic test. Doping La3+ into CeO2-ZrO2 solid solution could generate more oxygen vacancies, and could inhibit the sinter of CeO2-ZrO2 solid solution when calcined at high temperatures (800, 900 and 1000 °C). The washcoat Ce0.8Zr0.15La0.05Oδ had much better redox properties. The reductive temperature of Ce4+ species shifted to low temperature by 60 °C when the washcoats calcined at high temperatures (800, 900 and 1000 °C). The Pd/Ce0.8Zr0.15La0.05Oδ/substrate monolithic catalyst calcination at 500 °C had the best catalytic activity and the 95% toluene conversion at a temperature as low as 190 °C. When calcined at low temperature (500 and 700 °C), the catalytic activity has little improvement, however, when calcined at high temperature, the catalytic activity of Pd/Ce0.8Zr0.15La0.05Oδ/substrate monolithic catalysts had significant improvement. As catalyst washcoat, the Ce0.8Zr0.15La0.05Oδ had better thermal stability than the washcoat Ce0.8Zr0.2O2, the developed Pd/Ce0.8Zr0.15La0.05Oδ/ substrate monolithic catalyst in this work was promising for eliminating Volatile organic compounds.展开更多
High-surface-area and well-ordered mesoporous Fe-incorporated SBA-15(xFe-SBA-15)and SBA-15-supported FeOx(yFeOx/SBA-15)with the Fe surface density between 0.09 to 1.11 Fe-atom/nm2have been prepared using the one-step ...High-surface-area and well-ordered mesoporous Fe-incorporated SBA-15(xFe-SBA-15)and SBA-15-supported FeOx(yFeOx/SBA-15)with the Fe surface density between 0.09 to 1.11 Fe-atom/nm2have been prepared using the one-step synthesis and incipient wetness impregnation methods,respectively.Physicochemical properties of these materials were characterized by means of numerous techniques,and their catalytic activities for the combustion of toluene were evaluated.It is found that the xFe-SBA-15 and yFeOx/SBA-15 samples possessed rod-or chain-like morphologies.The Fe species were of high dispersion when the Fe surface density was lower than0.76 Fe-atom/nm2in xFe-SBA-15 and 0.64 Fe-atom/nm2in yFeOx/SBA-15.At a similar Fe surface density and space velocity,the xFe-SBA-15 catalysts showed better activity than the yFeOx/SBA-15 catalysts,in which the xFe-SBA-15 catalyst with Fe surface density 0.59 Fe-atom/nm2performed the best.It is concluded that the good performance of the xFe-SBA-15 sample with Fe surface density0.59 Fe-atom/nm2was associated with its large surface area,high Fe species dispersion,and good low-temperature reducibility.展开更多
A Ce0.4Zr0.6O2 washcoat was prepared using an impregnation method, which acted as a host for the active Pd component to prepare a Pd-Ce0.4Zr0.6O2/substrate monolithic catalyst for toluene combustion. The catalyst was ...A Ce0.4Zr0.6O2 washcoat was prepared using an impregnation method, which acted as a host for the active Pd component to prepare a Pd-Ce0.4Zr0.6O2/substrate monolithic catalyst for toluene combustion. The catalyst was characterized by scanning electron microscopy （SEM）, Raman spectroscopy, Brunauner-Emmett-Teller （BET）, and carbon monoxide tonperature-programmed reduction （CO-TPR）. It was found that the washcoat had strong vibration-shock resistance according to an ultrasonic test. The Pd-Ce0.4Zr0.6O2/substrate monolithic catalyst calcined at 400 ℃ showed 95% toluene conversion at a temperature as low as 210 ℃. Furthermore, the lowest temperature for 95% toluene conversion was increased by 40℃ after the catalyst calcined at 900℃, indicating that the catalyst had good thermal stability. The results revealed that the developed catalyst in this study was promising for eliminating volatile organic compounds （VOCs）.展开更多
Cu-Mn, Cu-Mn-Ce, and Cu-Ce mixed-oxide catalysts were prepared by a citric acid sol-gel method and then characterized by XRD, BET, H_2-TPR and XPS analyses. Their catalytic properties were investigated in the toluene ...Cu-Mn, Cu-Mn-Ce, and Cu-Ce mixed-oxide catalysts were prepared by a citric acid sol-gel method and then characterized by XRD, BET, H_2-TPR and XPS analyses. Their catalytic properties were investigated in the toluene combustion reaction. Results showed that the Cu-Mn-Ce ternary mixed-oxide catalyst with 1：2：4 mole ratios had the highest catalytic activity, and 99% toluene conversion was achieved at temperatures below 220°C. In the Cu-Mn-Ce catalyst, a portion of Cu and Mn species entered into the Ce O2 fluorite lattice, which led to the formation of a ceria-based solid solution. Excess Cu and Mn oxides existed on the surface of the ceria-based solid solution. The coexistence of Cu-Mn mixed oxides and the ceria-based solid solution resulted in a better synergetic interaction than the Cu-Mn and Cu-Ce catalysts, which promoted catalyst reducibility, increased oxygen mobility, and enhanced the formation of abundant active oxygen species.展开更多
CeO2 is an important porous material with a wide range of applications in the abatement of volatile organic compounds （VOCs）. In this paper, we prepared a series of novel three-dimensional （3D） micro/nanostructure...CeO2 is an important porous material with a wide range of applications in the abatement of volatile organic compounds （VOCs）. In this paper, we prepared a series of novel three-dimensional （3D） micro/nanostructured CeO2 materials via a solvothermal method. Organic acid-assisted synthesis and inorganic acid post-treatment were used to adjust the Ce02 microstructures. The size of the 3D micro/nanostructures could be controlled in the range from 180nm to 1.5 μm and the surface morphology changed from rough to smooth with the use of different organic acids. The CeO2 synthesized with acetic acid featured a hierarchical porosity and showed good performance for toluene catalytic combustion： a T50 of 187 ℃ and a T90 of 195 ℃. Moreover, the crystallite size, textural properties, and surface chemical states could be tuned by inorganic acid modification. After treatment with HNO3, the modified CeO2 materials exhibited improved catalytic activity, with a T50 of-175 ℃ and a T90 of -187 ℃. We concluded that the toluene combustion activity is related to the porosity and the amount of surface active oxygen of the CeO2. Both these features can be tuned by the co-work of organic and inorganic acids.展开更多
基金Project supported by Zhejiang Provincial Natural Science Foundation of China (203147)the National Natural Science Foundation of China (20473075)
文摘Two novel washcoats Ce0.8Zr0.15La0.05Oδ and Ce0.8Zr0.2O2 was prepared by an impregnation method, which acted as a host for the active Pd component to prepare Pd/Ce0.8Zr0.15La0.05Oδ/substrate and Pd/Ce0.8Zr0.2O2/substrate monolithic catalysts for toluene combustion. The washcoats was characterized by X-ray diffraction (XRD), Raman spectroscopy, Brunauner-Emmett-Teller (BET), and H2-temperature-programmed reduction (H2-TPR). The result indicated that both the washcoats had strong vibration-shock resistance according to ultrasonic test. Doping La3+ into CeO2-ZrO2 solid solution could generate more oxygen vacancies, and could inhibit the sinter of CeO2-ZrO2 solid solution when calcined at high temperatures (800, 900 and 1000 °C). The washcoat Ce0.8Zr0.15La0.05Oδ had much better redox properties. The reductive temperature of Ce4+ species shifted to low temperature by 60 °C when the washcoats calcined at high temperatures (800, 900 and 1000 °C). The Pd/Ce0.8Zr0.15La0.05Oδ/substrate monolithic catalyst calcination at 500 °C had the best catalytic activity and the 95% toluene conversion at a temperature as low as 190 °C. When calcined at low temperature (500 and 700 °C), the catalytic activity has little improvement, however, when calcined at high temperature, the catalytic activity of Pd/Ce0.8Zr0.15La0.05Oδ/substrate monolithic catalysts had significant improvement. As catalyst washcoat, the Ce0.8Zr0.15La0.05Oδ had better thermal stability than the washcoat Ce0.8Zr0.2O2, the developed Pd/Ce0.8Zr0.15La0.05Oδ/ substrate monolithic catalyst in this work was promising for eliminating Volatile organic compounds.
基金supported by the National Natural Science Foundation of China (21103005)the Natural Science Foundation of Beijing Municipality (2132015)the Discipline and Postgraduate Education Foundation (20111000501,005000542513551)
文摘High-surface-area and well-ordered mesoporous Fe-incorporated SBA-15(xFe-SBA-15)and SBA-15-supported FeOx(yFeOx/SBA-15)with the Fe surface density between 0.09 to 1.11 Fe-atom/nm2have been prepared using the one-step synthesis and incipient wetness impregnation methods,respectively.Physicochemical properties of these materials were characterized by means of numerous techniques,and their catalytic activities for the combustion of toluene were evaluated.It is found that the xFe-SBA-15 and yFeOx/SBA-15 samples possessed rod-or chain-like morphologies.The Fe species were of high dispersion when the Fe surface density was lower than0.76 Fe-atom/nm2in xFe-SBA-15 and 0.64 Fe-atom/nm2in yFeOx/SBA-15.At a similar Fe surface density and space velocity,the xFe-SBA-15 catalysts showed better activity than the yFeOx/SBA-15 catalysts,in which the xFe-SBA-15 catalyst with Fe surface density 0.59 Fe-atom/nm2performed the best.It is concluded that the good performance of the xFe-SBA-15 sample with Fe surface density0.59 Fe-atom/nm2was associated with its large surface area,high Fe species dispersion,and good low-temperature reducibility.
基金Project supported by Zhejiang Provincial Nature Science Foundation of China (203147)the National Natural ScienceFoundation of China (20473075)
文摘A Ce0.4Zr0.6O2 washcoat was prepared using an impregnation method, which acted as a host for the active Pd component to prepare a Pd-Ce0.4Zr0.6O2/substrate monolithic catalyst for toluene combustion. The catalyst was characterized by scanning electron microscopy （SEM）, Raman spectroscopy, Brunauner-Emmett-Teller （BET）, and carbon monoxide tonperature-programmed reduction （CO-TPR）. It was found that the washcoat had strong vibration-shock resistance according to an ultrasonic test. The Pd-Ce0.4Zr0.6O2/substrate monolithic catalyst calcined at 400 ℃ showed 95% toluene conversion at a temperature as low as 210 ℃. Furthermore, the lowest temperature for 95% toluene conversion was increased by 40℃ after the catalyst calcined at 900℃, indicating that the catalyst had good thermal stability. The results revealed that the developed catalyst in this study was promising for eliminating volatile organic compounds （VOCs）.
基金supported by the National Natural Science Foundation of China (21377008)2013 Education and Teaching-Postgraduate Students Education-2011 Beijing Municipality Excellent Ph.D.Thesis Supervisor (20111000501)+1 种基金2013 Education and Teaching-Postgraduate Students Cultivation-National Excellent Ph.D.Thesis Supervisor and Cultivation Base Construction (005000542513551)the Foundation on the Creative Research Team Construction Promotion Project of Beijing Municipal Institutions~~
文摘采用乙二胺辅助的水热法制备了纳米片聚结的Co3O4微球.利用多种分析技术表征了其物化性质,并评价了其对甲苯燃烧的催化活性.结果表明,由添加1.0 ml乙二胺经140°C水热处理12 h后制得的Co3O4样品呈纳米片聚结的微球状表面形貌.Co3O4微球样品的比表面积约为66 m2g-1.与体相Co3O4样品相比,Co3O4微球样品具有较高的氧吸附物种浓度和较好的低温还原性.当空速为20000 ml g-1h-1时,在Co3O4微球样品上甲苯转化率达到50%和90%时的反应温度分别为230和254°C.这与该样品具有较大的比表面积、较高的氧吸附物种浓度和较好的低温还原性相关.
基金the financial support from the Natural Science Foundation of China (No. 21107096)Zhejiang Provincial Natural Science Foundation of China (No. Y14E080008)+1 种基金the Commission of Science and Technology of Zhejiang province (No. 2013C03021)the Specialized Research Fund for the Doctoral Program of Higher Education (No. 20133317110004)
文摘Cu-Mn, Cu-Mn-Ce, and Cu-Ce mixed-oxide catalysts were prepared by a citric acid sol-gel method and then characterized by XRD, BET, H_2-TPR and XPS analyses. Their catalytic properties were investigated in the toluene combustion reaction. Results showed that the Cu-Mn-Ce ternary mixed-oxide catalyst with 1：2：4 mole ratios had the highest catalytic activity, and 99% toluene conversion was achieved at temperatures below 220°C. In the Cu-Mn-Ce catalyst, a portion of Cu and Mn species entered into the Ce O2 fluorite lattice, which led to the formation of a ceria-based solid solution. Excess Cu and Mn oxides existed on the surface of the ceria-based solid solution. The coexistence of Cu-Mn mixed oxides and the ceria-based solid solution resulted in a better synergetic interaction than the Cu-Mn and Cu-Ce catalysts, which promoted catalyst reducibility, increased oxygen mobility, and enhanced the formation of abundant active oxygen species.
基金This work was financially supported by the Natural Science Foundation of China （21576054）, the Scientific Project of Guangdong Province （2014A010106030, 2016A010104017,2016B020241003）, and the Foundation of Higher Education of Guangdong Province （201 SICFSCX027） of China.
文摘CeO2 is an important porous material with a wide range of applications in the abatement of volatile organic compounds （VOCs）. In this paper, we prepared a series of novel three-dimensional （3D） micro/nanostructured CeO2 materials via a solvothermal method. Organic acid-assisted synthesis and inorganic acid post-treatment were used to adjust the Ce02 microstructures. The size of the 3D micro/nanostructures could be controlled in the range from 180nm to 1.5 μm and the surface morphology changed from rough to smooth with the use of different organic acids. The CeO2 synthesized with acetic acid featured a hierarchical porosity and showed good performance for toluene catalytic combustion： a T50 of 187 ℃ and a T90 of 195 ℃. Moreover, the crystallite size, textural properties, and surface chemical states could be tuned by inorganic acid modification. After treatment with HNO3, the modified CeO2 materials exhibited improved catalytic activity, with a T50 of-175 ℃ and a T90 of -187 ℃. We concluded that the toluene combustion activity is related to the porosity and the amount of surface active oxygen of the CeO2. Both these features can be tuned by the co-work of organic and inorganic acids.