The thermodynamic parameters of FRW fire-retardant plywood at different temperatures were measured by dynamic mechanical analysis (DMA) equipment such as storage modulus, loss modulus and loss angle tangent. The influ...The thermodynamic parameters of FRW fire-retardant plywood at different temperatures were measured by dynamic mechanical analysis (DMA) equipment such as storage modulus, loss modulus and loss angle tangent. The influences on the thermodynamic properties of FRW fire-retardant plywood by the FRW fire retardant were analyzed between the FRW fire-retardant plywood and the untreated plywood. The results showed that the transition temperature of FRW fire-retardant plywood’s storage modulus was delayed than the untreated plywood. Its value was also higher than the untreated plywood. Meanwhile the glass transition temperature of plywood treated by FRW fire retardant was raised. FRW fire-retardant plywood could keep the better mechanical performances and ability of deformation-resistance at higher temperature and during longer period than the untreated plywood.展开更多
R513A是由R134a/R1234yf(质量分数比为56∶44)组成的新型环保制冷剂,其全球变暖潜能(GWP)值低,不可燃。选择混合制冷剂R513A作为研究对象,在原R134a家用电冰箱中进行制冷剂的替代实验研究。实验依据标准BS EN ISO 15502—2005中规定的...R513A是由R134a/R1234yf(质量分数比为56∶44)组成的新型环保制冷剂,其全球变暖潜能(GWP)值低,不可燃。选择混合制冷剂R513A作为研究对象,在原R134a家用电冰箱中进行制冷剂的替代实验研究。实验依据标准BS EN ISO 15502—2005中规定的工况进行,主要从降温时间、耗电量和冷冻能力三方面对R513A在电冰箱中的性能进行评估并与R134a进行对比。实验结果表明:最佳充注量下,R513A降温时间相比R134a降低21%;24h耗电量实验中相比R134a,R513A系统耗电量降低了3.5%,系统稳定运行时R513A的启停率小于R134a;冷冻能力实验中,同一工况下M包达到相同设定温度,R513A比R134a用时少约42.3min。此外在系统稳定运行时,R513A的系统排气温度低于R134a,其他参数和R134a很接近。通过对比实验可知,在未对原冰箱系统进行任何改动的情况下,R513A可以作为R134a的替代制冷剂直接充注到系统中使用。展开更多
文摘The thermodynamic parameters of FRW fire-retardant plywood at different temperatures were measured by dynamic mechanical analysis (DMA) equipment such as storage modulus, loss modulus and loss angle tangent. The influences on the thermodynamic properties of FRW fire-retardant plywood by the FRW fire retardant were analyzed between the FRW fire-retardant plywood and the untreated plywood. The results showed that the transition temperature of FRW fire-retardant plywood’s storage modulus was delayed than the untreated plywood. Its value was also higher than the untreated plywood. Meanwhile the glass transition temperature of plywood treated by FRW fire retardant was raised. FRW fire-retardant plywood could keep the better mechanical performances and ability of deformation-resistance at higher temperature and during longer period than the untreated plywood.
文摘R513A是由R134a/R1234yf(质量分数比为56∶44)组成的新型环保制冷剂,其全球变暖潜能(GWP)值低,不可燃。选择混合制冷剂R513A作为研究对象,在原R134a家用电冰箱中进行制冷剂的替代实验研究。实验依据标准BS EN ISO 15502—2005中规定的工况进行,主要从降温时间、耗电量和冷冻能力三方面对R513A在电冰箱中的性能进行评估并与R134a进行对比。实验结果表明:最佳充注量下,R513A降温时间相比R134a降低21%;24h耗电量实验中相比R134a,R513A系统耗电量降低了3.5%,系统稳定运行时R513A的启停率小于R134a;冷冻能力实验中,同一工况下M包达到相同设定温度,R513A比R134a用时少约42.3min。此外在系统稳定运行时,R513A的系统排气温度低于R134a,其他参数和R134a很接近。通过对比实验可知,在未对原冰箱系统进行任何改动的情况下,R513A可以作为R134a的替代制冷剂直接充注到系统中使用。