The oxidation behavior of 316L austenitic steel after thermal aging process at 600℃for 6 h was investigated in the supercritical water(600℃/25 MPa)with 1000 h.Results showed that the grain size and the proportion of...The oxidation behavior of 316L austenitic steel after thermal aging process at 600℃for 6 h was investigated in the supercritical water(600℃/25 MPa)with 1000 h.Results showed that the grain size and the proportion of high angle grain boundaries(HAGB)increased in the steel after thermal aging process,with the observation of micro-textures.The weight gain rate of the steel after aging process increased,presenting the decreased Cr_(2)O_(3)contain in the oxide layer,which resulted in the increasing diffusion rate of Fe and O ions in oxide layer.The molecular dynamics simulation results confirmed the high oxidation rate in HAGB and micro-textures for the 316L steel after aging process.展开更多
基金supported by the Hebei Natural Science Foundation(E2023502105)the China Postdoctoral Science Foundation(2023M741155)the Fundamental Research Funds for the Central Universities(JB2023030).
文摘The oxidation behavior of 316L austenitic steel after thermal aging process at 600℃for 6 h was investigated in the supercritical water(600℃/25 MPa)with 1000 h.Results showed that the grain size and the proportion of high angle grain boundaries(HAGB)increased in the steel after thermal aging process,with the observation of micro-textures.The weight gain rate of the steel after aging process increased,presenting the decreased Cr_(2)O_(3)contain in the oxide layer,which resulted in the increasing diffusion rate of Fe and O ions in oxide layer.The molecular dynamics simulation results confirmed the high oxidation rate in HAGB and micro-textures for the 316L steel after aging process.