Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nit...Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature.展开更多
The CaCu3Ti4O12(CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process(synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and ...The CaCu3Ti4O12(CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process(synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investigated. The phase composition was determined by X-ray diffraction and the microstructure was examined by SEM. The dielectric constant, dielectric loss, and resistance of the ceramic were also determined by a precision impedance tester. The results show that, as the synthesis temperature increases, the CCTO ceramic grain size decreases and the stoichiometric ratio of Cu/Ca at the grain boundary increases, the dielectric constant increases and the dielectric loss decreases(40 < f < 10 kHz). In addition, when the synthesis time is shorter than 12 h, the Cu/Ca ratio of CCTO decreases and the dielectric constant increases with time increase. However, when the synthesis time exceeds 12 h, this trend is just the opposite. It is further proved that Cu at the grain boundary is not conducive to the dielectric constant of CCTO.展开更多
MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties o...MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties of MAPO-11 molecular sieves was examined. The samples were characterized by the techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric/differential thermogravimetric analysis (TG-DGA), etc. The results show that the shape and size of crystal were influenced by the precursor of Mg, the Mg/Al ratio and the type of template, and the TG-DGA analysis shows that MAPO-11 molecular sieves as-synthesized have poor thermal stability.展开更多
基金Supported by the National Natural Science Foundation of China (Grant Nos. 50572032, 50731006)
文摘Type Ib diamonds were grown by the temperature gradient method (TGM) at 5.5 GPa and 1500-1560 K in a china-type cubic anvil high pressure apparatus using Ni70Mn25Co5 alloy as solvent/catalyst. The concentration of nitrogen (CN) in type Ib diamonds synthesized at different synthesis temperatures was measured by a Fourier transform infrared (FTIR) spectrometer. The dependence of CN in diamond on synthesis temperature was studied. For the type Ib diamonds synthesized using Ni70Mn25Co5 as catalyst, its CN decreases along with the increase of synthesis temperature.
文摘The CaCu3Ti4O12(CCTO) ceramic was prepared through conventional solid-state method. The effects of synthesis process(synthesis temperature and synthesis time) of powder on ceramic microstructures, CuO segregation and electrical properties were investigated. The phase composition was determined by X-ray diffraction and the microstructure was examined by SEM. The dielectric constant, dielectric loss, and resistance of the ceramic were also determined by a precision impedance tester. The results show that, as the synthesis temperature increases, the CCTO ceramic grain size decreases and the stoichiometric ratio of Cu/Ca at the grain boundary increases, the dielectric constant increases and the dielectric loss decreases(40 < f < 10 kHz). In addition, when the synthesis time is shorter than 12 h, the Cu/Ca ratio of CCTO decreases and the dielectric constant increases with time increase. However, when the synthesis time exceeds 12 h, this trend is just the opposite. It is further proved that Cu at the grain boundary is not conducive to the dielectric constant of CCTO.
文摘MAPO-11 molecular sieves were synthesized by hydrothermal methods. The influence of precursor of magnesium, Mg/Al ratio, synthesis temperature, synthesis time and the type of template on the formation and properties of MAPO-11 molecular sieves was examined. The samples were characterized by the techniques of X-ray diffraction (XRD), scanning electron microscopy (SEM), thermogravimetric/differential thermogravimetric analysis (TG-DGA), etc. The results show that the shape and size of crystal were influenced by the precursor of Mg, the Mg/Al ratio and the type of template, and the TG-DGA analysis shows that MAPO-11 molecular sieves as-synthesized have poor thermal stability.