TiO2 nanofibrils were prepared within the pores of alumina template membrane by use of sol-gel chemistry. The TiO2 nanofibrils have good crystallinity and size. There is agglomeration free among the particulates of ...TiO2 nanofibrils were prepared within the pores of alumina template membrane by use of sol-gel chemistry. The TiO2 nanofibrils have good crystallinity and size. There is agglomeration free among the particulates of TiO2 and the fibrils show high catalytic activity.展开更多
The organically templated titanium phosphate [Ti 3P 6O 27 H 5] · [C 2H 9N 2] 5·2 [H 3O] has been synthesized by solvothermal method and its structure was determined by single crystal X ray diffraction. The c...The organically templated titanium phosphate [Ti 3P 6O 27 H 5] · [C 2H 9N 2] 5·2 [H 3O] has been synthesized by solvothermal method and its structure was determined by single crystal X ray diffraction. The crystal crystallizes in a orthorhombic system of the enantiomorphic space group P 2 12 12 1 , with a = 1.018 0(6) nm , b =1.589 9(9) nm, c =2.322 7(12) nm, V =3.759 4(4) nm 3, Z =4, D c= 1.96 g/cm 3 , F (000)= 2 296 , R =0.048 6, ωR 2=0.125 7. The title compound contains chiral spirals formed from macroanionic chains of titanium oxygen octahedra bonded together by phosphate tetrahedral. These spirals are interconnected through hydrogen bonding in a manner to form unusual tunnels along the [001] direction in which H 2N(CH 2) 2NH 3 + cations are included. Second harmonics are generated in powdered sample. [WT5HZ]展开更多
PEDOT nanotubes were prepared by a template synthesis method. Based on our template, it was deduced that there are two successive processes in the formation of nanotubes. The first step is soakage of the porous templa...PEDOT nanotubes were prepared by a template synthesis method. Based on our template, it was deduced that there are two successive processes in the formation of nanotubes. The first step is soakage of the porous templates by a polymer solution, and the second step is adsorption of free charged cationic groups and doped PEDOT onto the template surface with negative charges. XRD results showed that well orientated PEDOT chains were formed during the synthesis, moreover the arrange conductivity of molecular chains strongly affect the structures of PEDOT nanotubes. The nanotubes were measured to be about 5.5-17.6 S/cm, which is higher than that of nanotube pellet due to the high contact resistance between the adjacent nanotubes.展开更多
基金supported by the National Natural Science Foundation of China(No 69890220)
文摘TiO2 nanofibrils were prepared within the pores of alumina template membrane by use of sol-gel chemistry. The TiO2 nanofibrils have good crystallinity and size. There is agglomeration free among the particulates of TiO2 and the fibrils show high catalytic activity.
文摘The organically templated titanium phosphate [Ti 3P 6O 27 H 5] · [C 2H 9N 2] 5·2 [H 3O] has been synthesized by solvothermal method and its structure was determined by single crystal X ray diffraction. The crystal crystallizes in a orthorhombic system of the enantiomorphic space group P 2 12 12 1 , with a = 1.018 0(6) nm , b =1.589 9(9) nm, c =2.322 7(12) nm, V =3.759 4(4) nm 3, Z =4, D c= 1.96 g/cm 3 , F (000)= 2 296 , R =0.048 6, ωR 2=0.125 7. The title compound contains chiral spirals formed from macroanionic chains of titanium oxygen octahedra bonded together by phosphate tetrahedral. These spirals are interconnected through hydrogen bonding in a manner to form unusual tunnels along the [001] direction in which H 2N(CH 2) 2NH 3 + cations are included. Second harmonics are generated in powdered sample. [WT5HZ]
基金Funded National Natural Science Foundation of China(No.: 60372002)
文摘PEDOT nanotubes were prepared by a template synthesis method. Based on our template, it was deduced that there are two successive processes in the formation of nanotubes. The first step is soakage of the porous templates by a polymer solution, and the second step is adsorption of free charged cationic groups and doped PEDOT onto the template surface with negative charges. XRD results showed that well orientated PEDOT chains were formed during the synthesis, moreover the arrange conductivity of molecular chains strongly affect the structures of PEDOT nanotubes. The nanotubes were measured to be about 5.5-17.6 S/cm, which is higher than that of nanotube pellet due to the high contact resistance between the adjacent nanotubes.