Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB...Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB） via nucleophilic substitution polymerization, which were subsequently used to fabricate ultrafiltration membrane by phase-inversion method for high temperature condensed water treatment. The obtained high molecular weight co-polymers with fluorene group with good solubility and good thermal stability, can be easily cast into flexible, white and non-transparent fiat films. The influence of molar ratio of BPA and BHPF on the properties of the prepared co-polymers and membranes was investigated in detail. SEM study of the morphology of the membranes indicated that the prepared membranes possessed homogeneous pores on the top surface and were sponge-like or finger-like in cross-section. Pure water flux of the membranes increased from 71.87 L·m-2.h-1 to 247.65 L·m-2.h-1, while the retention of BSA decreased slightly, and the water contact angle decreased from 82.1 ° to 55.6° with the PVP concentration from 0 wt% to 10 wt%. With increasing concentration of PVP, the mechanical properties of membranes decreased, while the thermal stability increased. The permeate flux measurement showed that the PAESK membrane had the potential for high temperature condensed water treatment.展开更多
A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacem...A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.展开更多
基金financial support under Heilongjiang Postdoctoral Fund (No.LBH-Z09175)
文摘Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB） via nucleophilic substitution polymerization, which were subsequently used to fabricate ultrafiltration membrane by phase-inversion method for high temperature condensed water treatment. The obtained high molecular weight co-polymers with fluorene group with good solubility and good thermal stability, can be easily cast into flexible, white and non-transparent fiat films. The influence of molar ratio of BPA and BHPF on the properties of the prepared co-polymers and membranes was investigated in detail. SEM study of the morphology of the membranes indicated that the prepared membranes possessed homogeneous pores on the top surface and were sponge-like or finger-like in cross-section. Pure water flux of the membranes increased from 71.87 L·m-2.h-1 to 247.65 L·m-2.h-1, while the retention of BSA decreased slightly, and the water contact angle decreased from 82.1 ° to 55.6° with the PVP concentration from 0 wt% to 10 wt%. With increasing concentration of PVP, the mechanical properties of membranes decreased, while the thermal stability increased. The permeate flux measurement showed that the PAESK membrane had the potential for high temperature condensed water treatment.
基金This project was supported by the National Ninth Five-Year-Plan Key Project "The pilot-scale production and the applied development of polyaryl ether concerning phthalazinone moiety" (No. 97-564-01-07).
文摘A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.