The hydration characteristics by thermal analysis (DTA) were determined, and an isothermal calorimeter (IC) was used to study the pastes. The experimental results indicate: (1) The main hydration products of SSC are C...The hydration characteristics by thermal analysis (DTA) were determined, and an isothermal calorimeter (IC) was used to study the pastes. The experimental results indicate: (1) The main hydration products of SSC are C-S-H (I) gel with a low Ca/Si ratio, crystalline Thomsonite-type and AFt-type phases containing certain alkali cations; (2) No phases of the AFm-type and high alkaline Ca (OH)(2) in SSC system could benefit the hydrated cements to improve its strength and durability; (3) Crystalline Thomsonite-type and AFt-type phases containing Na+ will greatly reduce free alkali and alleviate the harmness of alkali aggregate reaction (AAR) in SSC system; (4) Similar to ordinary Portland cement (OPC), the hydration process of SSC could be classified into five stage: initial, induction, acceleration, deceleration and decay; (5) Regardless of the activator used, the apparent activation energy is higher with the increased slag in cement system, and the rising temperature could promote the hydration of SSC.展开更多
基金Funded by the State"the Ninth-Five-year Plan "Item (96-535-33-5)
文摘The hydration characteristics by thermal analysis (DTA) were determined, and an isothermal calorimeter (IC) was used to study the pastes. The experimental results indicate: (1) The main hydration products of SSC are C-S-H (I) gel with a low Ca/Si ratio, crystalline Thomsonite-type and AFt-type phases containing certain alkali cations; (2) No phases of the AFm-type and high alkaline Ca (OH)(2) in SSC system could benefit the hydrated cements to improve its strength and durability; (3) Crystalline Thomsonite-type and AFt-type phases containing Na+ will greatly reduce free alkali and alleviate the harmness of alkali aggregate reaction (AAR) in SSC system; (4) Similar to ordinary Portland cement (OPC), the hydration process of SSC could be classified into five stage: initial, induction, acceleration, deceleration and decay; (5) Regardless of the activator used, the apparent activation energy is higher with the increased slag in cement system, and the rising temperature could promote the hydration of SSC.