The influence of rare earth （RE） elements on the solidification process and eutectic transformation and mechanical properties of the high-V type cast, high-speed steel roll was studied. Test materials with different...The influence of rare earth （RE） elements on the solidification process and eutectic transformation and mechanical properties of the high-V type cast, high-speed steel roll was studied. Test materials with different RE additions were prepared on a horizontal centrifugal casting machine. The solidification process, eutectic structure transformation, carbide morphology, and the elements present, were all investigated by means of differential scanning calorimetry （DSC） and scanning electron microscopy energy dispersive spectrometry （SEM-EDS）. The energy produced by crack initiation and crack extension was analyzed using a digital impact test machine. It was found that rare earth elements increased the tensile strength of the steel by inducing crystallization of earlier eutectic γ-Fe during the solidification process, which in turn increased the solidification temperature and thinned the dendritic grains. Rare earth elements with large atomic radius changed the lattice parameters of the MC carbide by forming rare earth carbides. This had the effect of dispersing longpole M C carbides to provide carbide grains, thereby, reducing the formation of the gross carbide and making more V available, to increase the secondary hardening process and improve the hardness level. The presence of rare earth elements in the steel raised the impact toughness by changing the mechanism of MC carbide formation, thereby increasing the crack initiation energy.展开更多
The effect of rare earth elements on the thermal cracking resistance of high speed steel （HSS） rolls was investigated. Laser rapid heating was used for thermal fatigue experiments. Thermal cracks and microstructure ...The effect of rare earth elements on the thermal cracking resistance of high speed steel （HSS） rolls was investigated. Laser rapid heating was used for thermal fatigue experiments. Thermal cracks and microstructure were observed using metalloscopy and scanning electron microscopy. The results showed that thermal cracks initiated from the interface between the matrix and eutectic carbides （including M6C and M7C3 type carbides）,and propagated along the interface between the two phases. MC type carbides enriched with vanadium could prevent the propagation of thermal cracks. The presence of rare earth elements decreased the quantity of big eutectic carbides,and proportionally increased spherical and rod-shaped MC type carbide content. HSS0 （0.00% RE） had approximately three times the thermal cracking density of HSS3 （0.12 wt.% RE）. Rare earth elements were shown to significantly improve the microstructure and thermal cracking resistance of HSS rolls.展开更多
基金Project supported by"863"Project (2006AA03Z532)the National Natural Science Foundation of China (NSFC 50341050)
文摘The influence of rare earth （RE） elements on the solidification process and eutectic transformation and mechanical properties of the high-V type cast, high-speed steel roll was studied. Test materials with different RE additions were prepared on a horizontal centrifugal casting machine. The solidification process, eutectic structure transformation, carbide morphology, and the elements present, were all investigated by means of differential scanning calorimetry （DSC） and scanning electron microscopy energy dispersive spectrometry （SEM-EDS）. The energy produced by crack initiation and crack extension was analyzed using a digital impact test machine. It was found that rare earth elements increased the tensile strength of the steel by inducing crystallization of earlier eutectic γ-Fe during the solidification process, which in turn increased the solidification temperature and thinned the dendritic grains. Rare earth elements with large atomic radius changed the lattice parameters of the MC carbide by forming rare earth carbides. This had the effect of dispersing longpole M C carbides to provide carbide grains, thereby, reducing the formation of the gross carbide and making more V available, to increase the secondary hardening process and improve the hardness level. The presence of rare earth elements in the steel raised the impact toughness by changing the mechanism of MC carbide formation, thereby increasing the crack initiation energy.
基金Project supported by the National Natural Science Foundation of China (51071136)
文摘The effect of rare earth elements on the thermal cracking resistance of high speed steel （HSS） rolls was investigated. Laser rapid heating was used for thermal fatigue experiments. Thermal cracks and microstructure were observed using metalloscopy and scanning electron microscopy. The results showed that thermal cracks initiated from the interface between the matrix and eutectic carbides （including M6C and M7C3 type carbides）,and propagated along the interface between the two phases. MC type carbides enriched with vanadium could prevent the propagation of thermal cracks. The presence of rare earth elements decreased the quantity of big eutectic carbides,and proportionally increased spherical and rod-shaped MC type carbide content. HSS0 （0.00% RE） had approximately three times the thermal cracking density of HSS3 （0.12 wt.% RE）. Rare earth elements were shown to significantly improve the microstructure and thermal cracking resistance of HSS rolls.