The residual stress of T-joints for SUS304 stainless steel by YAG laser welding was measured by the method of hole-drilling,and the effects of heat treatment and hardness distribution of weld joints on the distributio...The residual stress of T-joints for SUS304 stainless steel by YAG laser welding was measured by the method of hole-drilling,and the effects of heat treatment and hardness distribution of weld joints on the distribution of residual stress for T-joints were analyzed.The results showed that the maximum of longitudinal residual tensile stress for T-joints was about 140MPa.The maximum of residual stress was not more than 40MPa after heat treatment,the peak of residual stress reduced obviously.The gradient of residual stress distribution was also reduced significantly.Strain hardening phenomenon occurred for T-joints,and the hardness of weld and heat affected zone was both higher than the hardness of base metal,the peak of hardness occurred in the fusion line.The effect of strain hardening phenomenon of weld and heat affected zone on the residual stress distribution of T-joints for SUS304 stainless steel was obvious,which made longitudinal residual tensile stress become higher.展开更多
This paper presents studies on the microstructure and mechanical properties of AISI 316L stainless steel and AISI 4340 low-alloy steel joints formed by the Nd:YAG laser welding process. The weld microstructures and he...This paper presents studies on the microstructure and mechanical properties of AISI 316L stainless steel and AISI 4340 low-alloy steel joints formed by the Nd:YAG laser welding process. The weld microstructures and heat affected zones (HAZs) were investigated. Austenitic microstructures were observed in all of the samples. The sizes of the HAZs changed when the heat input was varied, and the 316L sides exhibited a larger HAZ. The cooling rates were calculated by measuring the solidification dendrite arm spacing. It is shown that high cooling rates lead to an austenitic microstructure. Tensile tests were carried out, and the results revealed the tensile properties of both the base metals and the weldments. The hardness test results agreed well with the tensile test results.展开更多
对电解腐蚀在不锈钢焊接接头低倍金相检验中的运用进行研究,通过试验选定腐蚀溶液、腐蚀时间和输出电流等参数。结果表明:采用10 mL HNO_3+90 mL H_2O腐蚀溶液,输出电流2 A,在室温下腐蚀6 min,制备出清晰的不锈钢焊接接头低倍金相试样,...对电解腐蚀在不锈钢焊接接头低倍金相检验中的运用进行研究,通过试验选定腐蚀溶液、腐蚀时间和输出电流等参数。结果表明:采用10 mL HNO_3+90 mL H_2O腐蚀溶液,输出电流2 A,在室温下腐蚀6 min,制备出清晰的不锈钢焊接接头低倍金相试样,可清晰显示焊接接头各个区域。展开更多
文摘The residual stress of T-joints for SUS304 stainless steel by YAG laser welding was measured by the method of hole-drilling,and the effects of heat treatment and hardness distribution of weld joints on the distribution of residual stress for T-joints were analyzed.The results showed that the maximum of longitudinal residual tensile stress for T-joints was about 140MPa.The maximum of residual stress was not more than 40MPa after heat treatment,the peak of residual stress reduced obviously.The gradient of residual stress distribution was also reduced significantly.Strain hardening phenomenon occurred for T-joints,and the hardness of weld and heat affected zone was both higher than the hardness of base metal,the peak of hardness occurred in the fusion line.The effect of strain hardening phenomenon of weld and heat affected zone on the residual stress distribution of T-joints for SUS304 stainless steel was obvious,which made longitudinal residual tensile stress become higher.
文摘This paper presents studies on the microstructure and mechanical properties of AISI 316L stainless steel and AISI 4340 low-alloy steel joints formed by the Nd:YAG laser welding process. The weld microstructures and heat affected zones (HAZs) were investigated. Austenitic microstructures were observed in all of the samples. The sizes of the HAZs changed when the heat input was varied, and the 316L sides exhibited a larger HAZ. The cooling rates were calculated by measuring the solidification dendrite arm spacing. It is shown that high cooling rates lead to an austenitic microstructure. Tensile tests were carried out, and the results revealed the tensile properties of both the base metals and the weldments. The hardness test results agreed well with the tensile test results.