Background The low-temperature resistance aging performance of Yttria-stabilized tetragonal zirconia polycrystal （Y-TZP） is the key effective factor that influences the long-term success rate of prosthesis. The obje...Background The low-temperature resistance aging performance of Yttria-stabilized tetragonal zirconia polycrystal （Y-TZP） is the key effective factor that influences the long-term success rate of prosthesis. The objective of this study was to test and compare the aging performances for resisting low temperature of Lava Frame, Cercon Smart, and Upcera Yttria-stabilized zirconia core materials, via analyzing the micro and the crystal phases of the materials, and measure the three-point bending strength and the fracture toughness. Methods The three zirconia green bodies were prepared as 60 test samples for three-point bending strength and as 60 test samples for fracture toughness. The test samples for three-point bending strength and fracture toughness were assigned to five groups and were treated respectively for 0, 5, 10, 15, and 20 hours to observe the micro and the crystal phases of the test samples. Then the three-point bending strength and fracture toughness were tested by X-ray diffraction （XRD）. Results The m phase content of Lava Frame was raised from 7.70% to 13.01%; the m phase content of Cercon Smart was raised from 4.95% to 8.53%; and Lava Frame is raised from 10.84% to 35.18%. The three-point bending strengths of the three zirconia core materials were higher than 1100 MPa and the fracture toughness was higher than 3 MPa.m^1/2. The three-point bending strength and the fracture toughness of Upcra zirconia decreased the most, followed by Lava Frame, and then by Cercon Smart. Conclusion The aging resistance sequences of the three zirconia core materials are, from strong to weak, Cercon Smart, Lava Frame, and Upcera.展开更多
We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth ...We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth conditions were optimized and the structure of the as-grown crystals was characterized by X-ray diffraction.The transmittance of 15 mol.% yttria-stabilized cubic zirconia crystal was nearly 80% in the range of 400–1600 nm.The refractive indices were measured and fitted the Sellmeier equation whi...展开更多
文摘Background The low-temperature resistance aging performance of Yttria-stabilized tetragonal zirconia polycrystal （Y-TZP） is the key effective factor that influences the long-term success rate of prosthesis. The objective of this study was to test and compare the aging performances for resisting low temperature of Lava Frame, Cercon Smart, and Upcera Yttria-stabilized zirconia core materials, via analyzing the micro and the crystal phases of the materials, and measure the three-point bending strength and the fracture toughness. Methods The three zirconia green bodies were prepared as 60 test samples for three-point bending strength and as 60 test samples for fracture toughness. The test samples for three-point bending strength and fracture toughness were assigned to five groups and were treated respectively for 0, 5, 10, 15, and 20 hours to observe the micro and the crystal phases of the test samples. Then the three-point bending strength and fracture toughness were tested by X-ray diffraction （XRD）. Results The m phase content of Lava Frame was raised from 7.70% to 13.01%; the m phase content of Cercon Smart was raised from 4.95% to 8.53%; and Lava Frame is raised from 10.84% to 35.18%. The three-point bending strengths of the three zirconia core materials were higher than 1100 MPa and the fracture toughness was higher than 3 MPa.m^1/2. The three-point bending strength and the fracture toughness of Upcra zirconia decreased the most, followed by Lava Frame, and then by Cercon Smart. Conclusion The aging resistance sequences of the three zirconia core materials are, from strong to weak, Cercon Smart, Lava Frame, and Upcera.
基金supported by the National Natural Science Foundation of China (50672111)Shanghai Science and Technology Committee (08520513100)
文摘We reported the development of a Ф100 cm growth apparatus for skull melting growth of yttria-stabilized cubic zirconia(YSZ) crystals and more than 1000 kg crystals have been grown in the furnace each time.The growth conditions were optimized and the structure of the as-grown crystals was characterized by X-ray diffraction.The transmittance of 15 mol.% yttria-stabilized cubic zirconia crystal was nearly 80% in the range of 400–1600 nm.The refractive indices were measured and fitted the Sellmeier equation whi...