Poly(butylene carbonateXPBC) has significantly promising applications as a degradable material in the field of polymers, while its poor thermal performance and low crystallization rate are its main defects. To overcom...Poly(butylene carbonateXPBC) has significantly promising applications as a degradable material in the field of polymers, while its poor thermal performance and low crystallization rate are its main defects. To overcome these shortcomings, a series of poly(butylene carbonate-co-spirocyclic carbonateXPBSC) copolymers were synthesized from diphenyl carbonate, 1,4-butanediol and spiroglycol via two-step polycondensation reactions, using magnesium oxide as a catalyst. Differential scanning calorimetry(DSC) results indicated that the glass transition temperature(Tg) values of PBSC copolymers were enhanced from -19℃ to 56℃ with rising the spiroacetal moiety content. Thermogravimetric analysis(TGA) results showed that the resulting PBSCs have a higher thermal stability than that of poly(butylene carbonate). Wide angle X-ray diflraction(WXRD) patterns were characterized to investigate the crystallization behaviour of PBSCs. Tensile testing demonstrated that copolymerization of spiroacetal moieties into PBC chains imparted PBSC with favourable mechanical performance. Typically, PBSC 30 had a tensile modulus of (1735±430) MPa, a tensile strength of (42±5) MPa and an elongation of 504%±36%.展开更多
通过两步熔融缩聚法合成了一系列基于碳酸二苯酯、1,4-丁二醇、异山梨醇和螺二醇的三元共聚碳酸酯(PBISC),其结构和组成经 1 H NMR和 13 C NMR表征,并采用GPC、 TGA、 DSC、 WXRD和拉伸试验分别对PBISC的性能进行研究。结果表明:PBISC...通过两步熔融缩聚法合成了一系列基于碳酸二苯酯、1,4-丁二醇、异山梨醇和螺二醇的三元共聚碳酸酯(PBISC),其结构和组成经 1 H NMR和 13 C NMR表征,并采用GPC、 TGA、 DSC、 WXRD和拉伸试验分别对PBISC的性能进行研究。结果表明:PBISC共聚物的玻璃化转变温度为63~72 ℃, T d,max 值接近350 ℃, PBISC共聚物具有较低的结晶性能。展开更多
文摘Poly(butylene carbonateXPBC) has significantly promising applications as a degradable material in the field of polymers, while its poor thermal performance and low crystallization rate are its main defects. To overcome these shortcomings, a series of poly(butylene carbonate-co-spirocyclic carbonateXPBSC) copolymers were synthesized from diphenyl carbonate, 1,4-butanediol and spiroglycol via two-step polycondensation reactions, using magnesium oxide as a catalyst. Differential scanning calorimetry(DSC) results indicated that the glass transition temperature(Tg) values of PBSC copolymers were enhanced from -19℃ to 56℃ with rising the spiroacetal moiety content. Thermogravimetric analysis(TGA) results showed that the resulting PBSCs have a higher thermal stability than that of poly(butylene carbonate). Wide angle X-ray diflraction(WXRD) patterns were characterized to investigate the crystallization behaviour of PBSCs. Tensile testing demonstrated that copolymerization of spiroacetal moieties into PBC chains imparted PBSC with favourable mechanical performance. Typically, PBSC 30 had a tensile modulus of (1735±430) MPa, a tensile strength of (42±5) MPa and an elongation of 504%±36%.