Nanocrystals are emerging as key materials due to their novel shape-and size-dependent chemical and physical properties that differ drastically from their bulk counterparts.The main challenges in this field remain rat...Nanocrystals are emerging as key materials due to their novel shape-and size-dependent chemical and physical properties that differ drastically from their bulk counterparts.The main challenges in this field remain rationally controlled synthesis and large scale production.This article reviews recent progress in our laboratory related to solution-based synthesis of various nanostructures,including zero-dimensional(0-D)nanocrystals,1-D nanowires and nanorods,hollow structures,and superlattice materials.On the other hand,the essential goal for nanoresearchers is to achieve industrial applications of nanostructured materials.In the past decades,these fascinating materials have been widely used in many promising fields such as nanofabrication,nanodevices,nanobiology,and nanocatalysis.Herein,we focus on their applications as nanocatalysts and try to illustrate the main problems and future directions in this area based on our recent endeavors in catalytic applications of nanocrystals.展开更多
The microstructural evolution, mechanical properties and fracture mechanism of a Ti.5Al.5Mo.5V.3Cr.1Zr (Ti-55531) alloy after solution (760.820℃) plus aging (580.640℃) treatments were investigated. The results show ...The microstructural evolution, mechanical properties and fracture mechanism of a Ti.5Al.5Mo.5V.3Cr.1Zr (Ti-55531) alloy after solution (760.820℃) plus aging (580.640℃) treatments were investigated. The results show that the volume fraction of the primary α(αp) phase decreases with the increase of solution temperature, and the length of the secondary α phase (αs) decreases while its width increases with the increase of aging temperature. Yield and tensile strengths decrease with the increase of solution temperature, while increase with the increase of aging temperature. A good balance of tensile strength and ductility of the alloy is obtained under solution of 800℃ for 2 h plus aging of 640℃ for 8 h, in which the tensile strength is 1434 MPa and the elongation is 7.7%. The coarsening αs phase makes crack propagation paths deflected and tortuous, which increases the crack propagation resistance and improves the ductility and fracture toughness.展开更多
基金This work was supported by NSFC(90606006)the State Key Project of Fundamental Research for Nanoscience and Nanotechnology(2006CB932300)the Key Grant Project of the Ministry of Education of P.R.China(No.306020).
文摘Nanocrystals are emerging as key materials due to their novel shape-and size-dependent chemical and physical properties that differ drastically from their bulk counterparts.The main challenges in this field remain rationally controlled synthesis and large scale production.This article reviews recent progress in our laboratory related to solution-based synthesis of various nanostructures,including zero-dimensional(0-D)nanocrystals,1-D nanowires and nanorods,hollow structures,and superlattice materials.On the other hand,the essential goal for nanoresearchers is to achieve industrial applications of nanostructured materials.In the past decades,these fascinating materials have been widely used in many promising fields such as nanofabrication,nanodevices,nanobiology,and nanocatalysis.Herein,we focus on their applications as nanocatalysts and try to illustrate the main problems and future directions in this area based on our recent endeavors in catalytic applications of nanocrystals.
基金Project(SKLSP201853) supported by the Fund of the State Key Laboratory of Solidification Processing in NWPU,ChinaProject(51625505) supported by the National Science Fund for Distinguished Young Scholars of China+1 种基金Project(U1537203) supported by the Key Program Project of the Joint Fund of Astronomy and National Natural Science Foundation of ChinaProject(KYQD1801) supported by the Scientific Research Foundation of Tianjin University of Technology and Education,China
文摘The microstructural evolution, mechanical properties and fracture mechanism of a Ti.5Al.5Mo.5V.3Cr.1Zr (Ti-55531) alloy after solution (760.820℃) plus aging (580.640℃) treatments were investigated. The results show that the volume fraction of the primary α(αp) phase decreases with the increase of solution temperature, and the length of the secondary α phase (αs) decreases while its width increases with the increase of aging temperature. Yield and tensile strengths decrease with the increase of solution temperature, while increase with the increase of aging temperature. A good balance of tensile strength and ductility of the alloy is obtained under solution of 800℃ for 2 h plus aging of 640℃ for 8 h, in which the tensile strength is 1434 MPa and the elongation is 7.7%. The coarsening αs phase makes crack propagation paths deflected and tortuous, which increases the crack propagation resistance and improves the ductility and fracture toughness.