In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitroge...In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.展开更多
M, a particular industrial waste, was selected to detoxify chromium slag at a high temperature. The carbon remaining in M reduced Cr （ Ⅳ ） of Na2 CrO4 borne in the chromium slag to Cr （ Ⅲ ） in the solid phase re...M, a particular industrial waste, was selected to detoxify chromium slag at a high temperature. The carbon remaining in M reduced Cr （ Ⅳ ） of Na2 CrO4 borne in the chromium slag to Cr （ Ⅲ ） in the solid phase reaction, and its thermodynamics and kinetics were studied. The reduction process of Na2CrO4 by carbon produced CO, whiCh＇was endothermic. Under the experimental condition, the apparent activation energy was 4. 41 kJ·mol^-1 , the＇apparent order of reaction for Na2 CrO4 was equal to one, and the partial pressure of CO was only 0.22 Pa at 1 330℃.展开更多
基金financially supported by the National Natural Science Foundation of China(No.U1260202)the National Basic Research Priorities Program of China(No.2012CB720401)the State Key Laboratory of Solid Waste Reuse for Building Materials
文摘In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.
基金Item Sponsored by National Natural Science Foundation of China (50234040)
文摘M, a particular industrial waste, was selected to detoxify chromium slag at a high temperature. The carbon remaining in M reduced Cr （ Ⅳ ） of Na2 CrO4 borne in the chromium slag to Cr （ Ⅲ ） in the solid phase reaction, and its thermodynamics and kinetics were studied. The reduction process of Na2CrO4 by carbon produced CO, whiCh＇was endothermic. Under the experimental condition, the apparent activation energy was 4. 41 kJ·mol^-1 , the＇apparent order of reaction for Na2 CrO4 was equal to one, and the partial pressure of CO was only 0.22 Pa at 1 330℃.