Melting temperature, spreadability, mechanical properties and the microstructures of joints brazed with silver-base filler metals including different amounts of Ga and/or In were studied respectively in this paper, an...Melting temperature, spreadability, mechanical properties and the microstructures of joints brazed with silver-base filler metals including different amounts of Ga and/or In were studied respectively in this paper, and the results show that the melting temperature of the silver-base filler metals is decreased, spreadability of the silver-base filler metals is improved, and the microstructures of silver-base filh, r metals are refined obviously with the addition of Ga and/or In. Using copper and brass plates as base metal and brazing with flame method, the mechanical properties of the lap-joint and butt joint were also examined and analyzed respectively, and the results indicate that the fracture position of two kinds of brazed joints occurred on the base metal, except for the lap-joint of brass, which shows better mechanical properties of the joints brazed with the silver- based filler metals including Ga. For the lap-joint of brass, the tensile strength gradually increased with the increase of Ga content, while the addition of In has little effect on mechanical properties. It is also found that the best comprehensive properties of cadmium-free Ag-Cu-Zn filler metals are obtained when Ga content is about 3.0 wt. % and In content is between 1.5 wt. % and 2. 0 wt. %.展开更多
采用液态单辊急冷法,在大气下制备了几种非晶态新型代银钎料箔带,其材料的最佳成分数w(Cu)为68%～79%,w(Ni)为5%～14%,w(Sn)为4%～10%,w(P)为7%.在反复实验的基础上,确定了合理的钎料母合金熔炼工艺和单辊急冷法制备工艺,冷辊转速、喷...采用液态单辊急冷法,在大气下制备了几种非晶态新型代银钎料箔带,其材料的最佳成分数w(Cu)为68%～79%,w(Ni)为5%～14%,w(Sn)为4%～10%,w(P)为7%.在反复实验的基础上,确定了合理的钎料母合金熔炼工艺和单辊急冷法制备工艺,冷辊转速、喷嘴口尺寸、喷带的间隙和喷射压力是制备非晶态箔带的关键工艺参数.制得的几种非晶态新型代银钎料箔带成型性良好,对折180°不折断.并利用DTA,SEM及XRD等方法对Cu P非晶态钎料箔带的非晶形成能力及熔化特性进行了研究.结果表明,制备的Cu Ni Sn P非晶合金箔带熔点和润湿性与Ag基钎料接近.展开更多
文摘Melting temperature, spreadability, mechanical properties and the microstructures of joints brazed with silver-base filler metals including different amounts of Ga and/or In were studied respectively in this paper, and the results show that the melting temperature of the silver-base filler metals is decreased, spreadability of the silver-base filler metals is improved, and the microstructures of silver-base filh, r metals are refined obviously with the addition of Ga and/or In. Using copper and brass plates as base metal and brazing with flame method, the mechanical properties of the lap-joint and butt joint were also examined and analyzed respectively, and the results indicate that the fracture position of two kinds of brazed joints occurred on the base metal, except for the lap-joint of brass, which shows better mechanical properties of the joints brazed with the silver- based filler metals including Ga. For the lap-joint of brass, the tensile strength gradually increased with the increase of Ga content, while the addition of In has little effect on mechanical properties. It is also found that the best comprehensive properties of cadmium-free Ag-Cu-Zn filler metals are obtained when Ga content is about 3.0 wt. % and In content is between 1.5 wt. % and 2. 0 wt. %.
文摘采用液态单辊急冷法,在大气下制备了几种非晶态新型代银钎料箔带,其材料的最佳成分数w(Cu)为68%～79%,w(Ni)为5%～14%,w(Sn)为4%～10%,w(P)为7%.在反复实验的基础上,确定了合理的钎料母合金熔炼工艺和单辊急冷法制备工艺,冷辊转速、喷嘴口尺寸、喷带的间隙和喷射压力是制备非晶态箔带的关键工艺参数.制得的几种非晶态新型代银钎料箔带成型性良好,对折180°不折断.并利用DTA,SEM及XRD等方法对Cu P非晶态钎料箔带的非晶形成能力及熔化特性进行了研究.结果表明,制备的Cu Ni Sn P非晶合金箔带熔点和润湿性与Ag基钎料接近.
